Influence of Lightly Burned MgO on the Mechanical Properties and Anticarbonization of Cement-Based Materials

Abstract

This study aims to study the influence of a lightly burned magnesium oxide (LBMO) expansion agent on the rheological properties (the slump flow, plastic viscosity and variation of shear stress) of cement-based materials. Four different mass contents (i.e., 0%, 3%, 6% and 9%) of LBMO were selected. The following compressive strength and expansion value of the corresponding cement concrete were tested. Cement concrete with two strength grades of 30 MPa and 50 MPa (C30 and C50) was selected. Results indicated that the addition of LBMO can effectively decrease the fluidity and increase the plastic viscosity of fresh cement paste. An optimum dosage (3%) of LBMO is the most advantageous to the compressive strength of cement concrete. The addition of LBMO can increase the expansion rate of cement concrete, thus preventing inside cracks. Moreover, the incorporation of LBMO led to a reduction in the fluidity of the cement paste and an increase in plastic viscosity. The addition of LBMO can increase the expansion rate of cement concrete, thus preventing inside cracks. It can be found that little difference exists in the compressive strength and the expansion rate of cement concrete with strength grades of 30 MPa and 50 MPa. Finally, the increased dosage of LBMO, curing age and compressive strength led to improving the carbonization resistance of cement concrete.