Study on swelling behaviour of HANP/PVA composites with adding PLGA for alveolar ridge preservation

Feni Istikharoh, H. Sujuti, E. Mustamsir, Astika Swastirani
{"title":"Study on swelling behaviour of HANP/PVA composites with adding PLGA for alveolar ridge preservation","authors":"Feni Istikharoh, H. Sujuti, E. Mustamsir, Astika Swastirani","doi":"10.15562/jdmfs.v6i3.998","DOIUrl":null,"url":null,"abstract":"Objective: The aim of this study was to compare the swelling behaviour of HANP/PVA and HANP/PLGA/PVA composites. Material and Methods: This study was divided into 2 groups, HANP/ PVA and HANP/PLGA/PVA composites which prepared by freeze drying methods. HANP 20% (w/w) was combined with PLGA 20% (w/w) and dissolved in PVA solution at 50C. Swelling behaviour was obtained by measured initial weight (Wi) and the weight of composites after immersing in PBS pH 7.4; 37C for 7 days (Ws). Statistical analysis based on Independent T-test (p<0.05). Results: The initial weight (Wi) of HANP/PVA and HANP/PLGA/PVA composites are 467±4.73 and 292±9.52. The swollen weight (Ws) of HANP/PVA and HANP/PLGA/PVA composites are 897±26.61 and 860±32.36. Furthermore, the water retention of HANP/PVA composite is 92.07% (p<0.05) and HANP/PLGA/PVA composite is 194.52% (p<0.05). Conclusion: The addition of PLGA enhance swelling behaviour of HANP/PVA composites. The strong interaction between HANP and PVA decrease the swelling re. HANP is inert in nature, but the combination of HANP/PLGA/PVA can be a good substitute for alveolar preservation.","PeriodicalId":31119,"journal":{"name":"Journal of Dentomaxillofacial Science","volume":"23 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2021-12-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Dentomaxillofacial Science","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.15562/jdmfs.v6i3.998","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 0

Abstract

Objective: The aim of this study was to compare the swelling behaviour of HANP/PVA and HANP/PLGA/PVA composites. Material and Methods: This study was divided into 2 groups, HANP/ PVA and HANP/PLGA/PVA composites which prepared by freeze drying methods. HANP 20% (w/w) was combined with PLGA 20% (w/w) and dissolved in PVA solution at 50C. Swelling behaviour was obtained by measured initial weight (Wi) and the weight of composites after immersing in PBS pH 7.4; 37C for 7 days (Ws). Statistical analysis based on Independent T-test (p<0.05). Results: The initial weight (Wi) of HANP/PVA and HANP/PLGA/PVA composites are 467±4.73 and 292±9.52. The swollen weight (Ws) of HANP/PVA and HANP/PLGA/PVA composites are 897±26.61 and 860±32.36. Furthermore, the water retention of HANP/PVA composite is 92.07% (p<0.05) and HANP/PLGA/PVA composite is 194.52% (p<0.05). Conclusion: The addition of PLGA enhance swelling behaviour of HANP/PVA composites. The strong interaction between HANP and PVA decrease the swelling re. HANP is inert in nature, but the combination of HANP/PLGA/PVA can be a good substitute for alveolar preservation.
添加PLGA用于牙槽嵴保存的HANP/PVA复合材料膨胀行为研究
目的:比较HANP/PVA和HANP/PLGA/PVA复合材料的膨胀行为。材料与方法:本研究分为两组,分别是冷冻干燥法制备的HANP/ PVA和HANP/PLGA/PVA复合材料。HANP 20% (w/w)与PLGA 20% (w/w)混合,在50C的PVA溶液中溶解。在pH为7.4的PBS中浸泡后,通过测量初始重量(Wi)和复合材料的重量来获得膨胀行为;37℃,7天(Ws)。采用独立t检验进行统计学分析(p<0.05)。结果:HANP/PVA复合材料和HANP/PLGA/PVA复合材料的初始质量(Wi)分别为467±4.73和292±9.52。HANP/PVA和HANP/PLGA/PVA复合材料的膨胀质量(Ws)分别为897±26.61和860±32.36。HANP/PVA复合材料保水率为92.07% (p<0.05), HANP/PLGA/PVA复合材料保水率为194.52% (p<0.05)。结论:PLGA的加入增强了HANP/PVA复合材料的膨胀性能。HANP与PVA之间的强相互作用减少了肺泡的肿胀,HANP本身是惰性的,但HANP/PLGA/PVA的组合可以很好地替代肺泡的保存。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 求助全文
来源期刊
CiteScore
0.50
自引率
0.00%
发文量
0
审稿时长
16 weeks
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信