Preparation, Characterization and Photocatalysis Properties of Visible Spectral Response Photocatalyst CoPcS/TiO2/K2Ti4O9

Abstract

Photocatalyst CoPcS/TiO2 was prepared by sol-gel method. Composite CoPcS/TiO2/K2Ti4O9 was prepared by dipping. It was incandesced at various temperatures and modification effect was compared. The results showed that optical absorption of sample incandesce at 423K occurred significant red-shift. Light absorption width extended from ultraviolet region to visible region, especially there was an intensive absorption between 600 nm and 680 nm. X-ray diffraction spectrogram showed that TiO2 in sample still maintained anatase crystal form. Under the illumination of visible light, photocatalysis degradation experiment was taken with Orange II as simulated pollutants. Decoloration rate of Orange II was much improved. The rate can reach 85% in 300 minutes.