Characterization of Organic Polymer Monolith Columns Containing Ammonium Quarternary As Initial Study For Capillary Chromatography

Elkawnie Pub Date : 2021-06-30 DOI:10.22373/ekw.v7i1.8764

A. Rahayu, S. Jamilatun, J. A. Fajri, L. Lim

{"title":"Characterization of Organic Polymer Monolith Columns Containing Ammonium Quarternary As Initial Study For Capillary Chromatography","authors":"A. Rahayu, S. Jamilatun, J. A. Fajri, L. Lim","doi":"10.22373/ekw.v7i1.8764","DOIUrl":null,"url":null,"abstract":"Abstract: The polymerization process with a simple step has become the centre of attention of several researchers. Various polymers have been developed, although in general, they use polymerization with a post-modification method. A quaternary ammonium monolith organic polymer has been prepared using a simple single thermal method in this research. 2-(Methacryloyloxy)-N,N,N-trimethylethanaminium chloride was as the monomer, and ethylene dimethacrylate was as crosslinker. The polymerization proceeded in fused-silica capillary (100 mm, 0.32 mm i.d. x 0.45 mm o.d.) using a one-pot approach method. To achieve the perfect macropores, isopropyl alcohol, PEG 400, and ethanol were used as porogen. Characterization of the surface morphology was carried out using a Scanning Electron Microscope (SEM), and the existence of an amine group was characterized by Fourier Transform Infrared Spectroscopy (FTIR). The distribution size of pores in the polymer was in the range of 1.29 to 3.33 µm.Abstrak: Polimerisasi dengan proses yang sederhana dan simpel menjadi pusat perhatian beberapa peneliti. Berbagai macam polimer telah dikembangkan, akan tetapi pada umumnya menggunakan polimerisasi dengan metode post-modification. Pada penelitian ini, polimer organik yang mengandung amonium kuartener dalam bentuk monolit dengan polimerisasi yang menggunakan suhu tunggal dan sederhana telah dilakukan. 2-(Methacryloyloxy)-N,N,N-trimethylethanaminium chloride digunakan sebagai monomer dan ethylene dimethacrylate sebagai crosslinker. Polimerisasi dilakukan dengan metode one-pot aaproach di dalam kapiler silika (100 mm, 0,32 mm i.d. x 0,45 mm o.d.). Untuk mendapatkan makropori yang sempurna, isopropil alkohol, PEG 400 dan etanol digunakan sebagai porogen. Karakterisasi morfologi permukaan dilakukan dengan menggunakan Scanning Electron Microscope (SEM), dan Fourier Transform Infrared Spectroscopy (FTIR) untuk mengidentifikasi gugus fungsi gugus amina yang terdapat pada polimer. Ukuran distribusi pori pada polimer berkisar antara 1,29 sampai 3,33 µm.","PeriodicalId":11527,"journal":{"name":"Elkawnie","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2021-06-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Elkawnie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.22373/ekw.v7i1.8764","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 1

Abstract

Abstract: The polymerization process with a simple step has become the centre of attention of several researchers. Various polymers have been developed, although in general, they use polymerization with a post-modification method. A quaternary ammonium monolith organic polymer has been prepared using a simple single thermal method in this research. 2-(Methacryloyloxy)-N,N,N-trimethylethanaminium chloride was as the monomer, and ethylene dimethacrylate was as crosslinker. The polymerization proceeded in fused-silica capillary (100 mm, 0.32 mm i.d. x 0.45 mm o.d.) using a one-pot approach method. To achieve the perfect macropores, isopropyl alcohol, PEG 400, and ethanol were used as porogen. Characterization of the surface morphology was carried out using a Scanning Electron Microscope (SEM), and the existence of an amine group was characterized by Fourier Transform Infrared Spectroscopy (FTIR). The distribution size of pores in the polymer was in the range of 1.29 to 3.33 µm.Abstrak: Polimerisasi dengan proses yang sederhana dan simpel menjadi pusat perhatian beberapa peneliti. Berbagai macam polimer telah dikembangkan, akan tetapi pada umumnya menggunakan polimerisasi dengan metode post-modification. Pada penelitian ini, polimer organik yang mengandung amonium kuartener dalam bentuk monolit dengan polimerisasi yang menggunakan suhu tunggal dan sederhana telah dilakukan. 2-(Methacryloyloxy)-N,N,N-trimethylethanaminium chloride digunakan sebagai monomer dan ethylene dimethacrylate sebagai crosslinker. Polimerisasi dilakukan dengan metode one-pot aaproach di dalam kapiler silika (100 mm, 0,32 mm i.d. x 0,45 mm o.d.). Untuk mendapatkan makropori yang sempurna, isopropil alkohol, PEG 400 dan etanol digunakan sebagai porogen. Karakterisasi morfologi permukaan dilakukan dengan menggunakan Scanning Electron Microscope (SEM), dan Fourier Transform Infrared Spectroscopy (FTIR) untuk mengidentifikasi gugus fungsi gugus amina yang terdapat pada polimer. Ukuran distribusi pori pada polimer berkisar antara 1,29 sampai 3,33 µm.

查看原文本刊更多论文

含季铵盐有机聚合物整体柱的表征及其毛细管色谱的初步研究

摘要:步骤简单的聚合工艺已成为许多研究者关注的焦点。各种聚合物已经被开发出来，尽管一般来说，它们使用后改性方法聚合。本研究采用简单的单热法制备了季铵盐整体有机聚合物。以2-(甲基丙烯酰氧基)-N,N,N-三甲基乙胺氯为单体，二甲基丙烯酸乙酯为交联剂。在熔融石英毛细管(100 mm, 0.32 mm id x 0.45 mm od)中采用一锅法进行聚合。以异丙醇、peg400和乙醇为成孔剂，制备出完美的大孔。利用扫描电镜(SEM)对其表面形貌进行了表征，并用傅里叶变换红外光谱(FTIR)对其是否存在胺基进行了表征。聚合物的孔隙分布尺寸在1.29 ~ 3.33µm之间。摘要/ abstract摘要:本文提出了一种新的研究方法，即在不同的环境下，对不同的环境进行研究。Berbagai macam polymer telah dikembangkan, akan tetapi pada umumnya menggunakan polerisasi dengan method后修正。高分子有机，高分子有机，高分子有机，高分子有机，高分子有机，高分子有机2-(甲基丙烯酰氧基)-N,N,N-三甲基乙胺氯化钠二甲基丙烯酸乙酯单体和二甲基丙烯酸乙酯交联剂。用一锅法处理水稻(100mm, 0.32 mm长× 0.45 mm长)。Untuk mendapatkan makropori yang sempurna，异丙醇，peg400和乙醇，digunakan sebagai。扫描电子显微镜(SEM)、傅立叶变换红外光谱(FTIR)等技术研究了孟古那坎(menggunakan)聚合物。Ukuran distribubusi pori pada聚合物berkisar antara 1,29 sampai 3,33µm。