Ultra-fine ferrite grains obtained in the TSDR process

Abstract

By careful design of rolling schedule, ultra-fine (∼2 μm) ferrite grains in a low carbon high niobium (0.09wt%Nb) micro-alloying steel with average austenite grain sizes above 800 μm can be achieved in the simulated thin slab direct rolling process. The 5-pass deformation was divided into two stages: the refinement of austenite through complete recrystallization and the refinement of ferrite through dynamic strain-induced transformation. The effects of Nb in solution and strain-induced NbCN precipitates on the ferrite transformation were also extensively discussed.