Surface modification of polypropylene by chromylchloride

Abstract

The changes of the adhesion properties of isotactic polypropylene (iPP) modified by chromylchloride (CrCl) have been studied. The free surface energy (FSE) of the iPP increases with the time of the modification and reaches a constant value after the time which strongly depends on the temperature of the modification. A similar trend has been observed for the dependences of the FSE vs. concentration of carbonyl groups. The molecular weight of the modified iPP decreases with the temperature of modification. The decrease of the FSE with time is negligible. It was found that after modification of iPP with CrCl the increase of mechanical work of adhesion was higher by 36% than that with chromosulfuric acid. Die Anderungen der Adhasionseigenschaften von mit Chromylchlorid modifiziertem isotaktischem Polypropylen (iPP) wurden untersucht. Die freie Oberflachenenergie (FSE) des isotaktischen Polypropylens nimmt mit der Reaktionszeit zu und hangt stark von der Modifikationstemperatur ab. Gleiches gilt fur die Abhangigkeit der FSE von der Konzentration der Carbonylgruppen. Das Molekulargewicht des modifizierten iPP sinkt mit steigender Temperatur der Modifikation. Die Abnahme der FSE mit der Zeit ist gering. Nach der Modifizierung des iPP mit CrCl war der Zuwachs der mechanischen Adhasionsarbeit um 36% hoher als nach der Modifikation mit Chromschwefelsaure.