Microstructure studies in Nd2(Fe0.9Co0.1)14B thin films

Materials Science and Engineering Pub Date : 1988-03-01 DOI:10.1016/0025-5416(88)90312-6

J. Strzeszewski , A. Nazareth, G.C. Hadjipanayis, K. Aylesworth, Z.R. Zhao, D.J. Sellmyer

引用次数: 4

Abstract

Large coercive fields (above 10 kOe) have been produced in thin sputtered films of Nd(FeCo)B. The films were either deposited at room temperature and heat treated or deposited onto high-temperature substrates (to about 730 °C). Transmission electron microscopy was used to study the microstructure and magnetic domain structure of the films. Correlations were observed between sputtering and growth parameters, microstructure and magnetic properties.