Mechanical properties of nanostructured titanium prepared by cryogenic rolling

Q4 Materials Science

塑性工程学报 Pub Date : 2013-01-01 DOI:10.3969/J.ISSN.1007-2012.2013.06.003

Y. K. Li, F. Liu, G. Zheng

引用次数: 0

Abstract

Commercial-pure titanium(CP-Ti)was subjected to cryogenic rolling at liquid nitrogen temperatures.The microstructures of the samples were investigated by X-ray diffraction(XRD)and transmission electron microscopy(TEM).The mechanical properties of Ti prepared by cryogenic rolling were measured using nano-indentation.The experimental results showed that the mean grain size of Ti was refined from 57μm to 75nm after cryogenic rolling.The hardness of the nanostructured Ti is as high as 3.36GPa.

查看原文本刊更多论文

低温轧制制备纳米钛的力学性能

对商品纯钛(CP-Ti)在液氮温度下进行低温轧制。采用x射线衍射(XRD)和透射电子显微镜(TEM)研究了样品的微观结构。采用纳米压痕法对低温轧制制备的Ti的力学性能进行了测试。实验结果表明，低温轧制后Ti的平均晶粒尺寸由57μm细化到75nm。纳米结构Ti的硬度高达3.36GPa。