A qualitative, process-parameter-based model for the release agent transfer during CFRP-part production: an approach to increase the initial bondability
{"title":"A qualitative, process-parameter-based model for the release agent transfer during CFRP-part production: an approach to increase the initial bondability","authors":"David Blass, Sven Hartwig, Klaus Dilger","doi":"10.1186/s40563-017-0095-7","DOIUrl":null,"url":null,"abstract":"<p>Adhesive bonding shows a high potential to join carbon fiber reinforced plastics (CFRP), if the adhesion between adhesive and part surface is verified. Unfortunately, this adhesion is often reduced in case of the mold-based part production and its unavoidable application of release agents. Due to the resulting presence of release agent residues on the surface of the cured CFRP-parts the adhesion is lowered. To increase the bondability and correlating production efficiency, the amount of release agent transfer should be as small as possible, to reduce the effort in terms of bonding pre-treatment. To achieve this goal, a theoretical, qualitative model about the influence of the relevant processing parameters for a thermoset CFRP-production was developed focusing the (diffusion-based) transfer reduction based on an adapted processing. Indicating the time in which the diffusion is possible, as the main criteria.</p>","PeriodicalId":464,"journal":{"name":"Applied Adhesion Science","volume":"5 1","pages":""},"PeriodicalIF":1.6800,"publicationDate":"2017-09-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1186/s40563-017-0095-7","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Applied Adhesion Science","FirstCategoryId":"1085","ListUrlMain":"https://link.springer.com/article/10.1186/s40563-017-0095-7","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"Dentistry","Score":null,"Total":0}
引用次数: 0
Abstract
Adhesive bonding shows a high potential to join carbon fiber reinforced plastics (CFRP), if the adhesion between adhesive and part surface is verified. Unfortunately, this adhesion is often reduced in case of the mold-based part production and its unavoidable application of release agents. Due to the resulting presence of release agent residues on the surface of the cured CFRP-parts the adhesion is lowered. To increase the bondability and correlating production efficiency, the amount of release agent transfer should be as small as possible, to reduce the effort in terms of bonding pre-treatment. To achieve this goal, a theoretical, qualitative model about the influence of the relevant processing parameters for a thermoset CFRP-production was developed focusing the (diffusion-based) transfer reduction based on an adapted processing. Indicating the time in which the diffusion is possible, as the main criteria.
期刊介绍：
Applied Adhesion Science focuses on practical applications of adhesives, with special emphasis in fields such as oil industry, aerospace and biomedicine. Topics related to the phenomena of adhesion and the application of adhesive materials are welcome, especially in biomedical areas such as adhesive dentistry. Both theoretical and experimental works are considered for publication. Applied Adhesion Science is a peer-reviewed open access journal published under the SpringerOpen brand. The journal''s open access policy offers a fast publication workflow whilst maintaining rigorous peer review process.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号