EFFECT OF WATER ABSORPTION ON THE MECHANICAL PROPERTIES OF SILANE-TREATED WOOD FLOUR POLYPROPYLENE COMPOSITES

Abstract

The behavior of the wood flour-polypropylene composites prepared with various contents of untreated and silane-treated wood flour by immersion in water was studied, as well as the effect of the water absorbed by the samples on their mechanical properties. The highest degree of water absorption was observed for the composites containing 30 – 50 mass% alkali pre-treated wood flour. For the materials with 50 mass% untreated, silane-treated and alkali pre-treated wood flour, the water absorption measured was 8.76%, 7.84% and 13.91%, respectively, after 15 days immersion in water. The value of the thickness swelling calculated for the samples prepared with 50 mass% silane-treated wood flour – polypropylene was the lowest – 1.29%. It was proved that the absorption of water molecules results in change of the tensile profile of the thermoplastic polypropylene composites filled with hygroscopic filler.