Abnormal grain growth of 68Cu–16Al–16Zn alloys for elastocaloric cooling via cyclical heat treatments

Abstract

Cu-based superelastic shape memory alloys are promising for low-stress elastocaloric cooling. We have synthesized bulk alloys of 68Cu–16Al–16Zn under different conditions in order to promote its grain growth and enhance its elastocaloric properties. High-temperature x-ray diffraction of untreated 68Cu–16Al–16Zn alloy showed that the phase boundary between the α + β mixed phases and the high temperature phase (β phase) was between 973 K and 1023 K. Based on this result, the 68Cu–16Al–16Zn alloy was heated and cooled in a furnace repeatedly between 773 K and 1173 K. The maximum grain size after heat treatment of the ingot rolled to 67% reached 11.1 mm. The latent heat of the martensitic transformation after grain growth was 6.3 J g−1, which is higher than the previously reported value for the compound. The stress–strain curve of 68Cu–16Al–16Zn rolled to 67% rolling with cyclical heat treatments showed a maximum stress of 106 MPa at 4.5% strain, with adiabatic temperature change of 5.9 K in heating during stress loading and 5.6 K in cooling in stress removal. Furthermore, no fatigue in the stress–strain behavior was observed up to at least 60 000 mechanical cycles at 2% strain.