Fabrication and Performance Analysis of Porcelain Stoneware Tiles Incorporated With Labware Glass Cullet

IF 1.5 4区材料科学 Q3 MATERIALS SCIENCE, CERAMICS

Transactions of the Indian Ceramic Society Pub Date : 2021-01-02 DOI:10.1080/0371750X.2021.1873864

Md Jahidul Haque, Ahsan Habib Munna, Suhanur Rahman, Ma-ariz Rahman

{"title":"Fabrication and Performance Analysis of Porcelain Stoneware Tiles Incorporated With Labware Glass Cullet","authors":"Md Jahidul Haque, Ahsan Habib Munna, Suhanur Rahman, Ma-ariz Rahman","doi":"10.1080/0371750X.2021.1873864","DOIUrl":null,"url":null,"abstract":"This study reported the effects of labware glass cullet on the properties of porcelain stoneware tiles. Five formulations of porcelain stoneware tiles (containing 0, 3, 6, 9, 12% borosilicate glass cullet) were prepared by adopting three different sintering temperatures (1100o, 1150o, 1200oC). The physical, microstructural and mechanical properties were analyzed. X-ray diffraction analysis ensured the presence of different crystalline phases in the samples. Morphological analysis also confirmed the results obtained from the XRD analysis. However, the density of the specimens increased within their operating parameters. Addition of glass cullet in the tiles increased the kinetics of the sintering process resulting in lower open porosity. Water absorption value of the samples sintered at 1200oC remained within the tolerance limit (∼0.5%). The lowest water absorption value (∼0.10%) as well as the highest linear shrinkage value (∼8.9%) were observed in the sample containing 12% glass cullet. Moreover, the usages of 12% glass cullet resulted in improved mechanical properties in comparison with other synthesized samples, whereas the values of compressive strength, impact strength and hardness were 51.65 MPa, 36.90 psi and 7.22 MPa, respectively. GRAPHICAL ABSTRACT","PeriodicalId":23233,"journal":{"name":"Transactions of the Indian Ceramic Society","volume":null,"pages":null},"PeriodicalIF":1.5000,"publicationDate":"2021-01-02","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1080/0371750X.2021.1873864","citationCount":"1","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Transactions of the Indian Ceramic Society","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1080/0371750X.2021.1873864","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, CERAMICS","Score":null,"Total":0}

引用次数: 1

Abstract

This study reported the effects of labware glass cullet on the properties of porcelain stoneware tiles. Five formulations of porcelain stoneware tiles (containing 0, 3, 6, 9, 12% borosilicate glass cullet) were prepared by adopting three different sintering temperatures (1100o, 1150o, 1200oC). The physical, microstructural and mechanical properties were analyzed. X-ray diffraction analysis ensured the presence of different crystalline phases in the samples. Morphological analysis also confirmed the results obtained from the XRD analysis. However, the density of the specimens increased within their operating parameters. Addition of glass cullet in the tiles increased the kinetics of the sintering process resulting in lower open porosity. Water absorption value of the samples sintered at 1200oC remained within the tolerance limit (∼0.5%). The lowest water absorption value (∼0.10%) as well as the highest linear shrinkage value (∼8.9%) were observed in the sample containing 12% glass cullet. Moreover, the usages of 12% glass cullet resulted in improved mechanical properties in comparison with other synthesized samples, whereas the values of compressive strength, impact strength and hardness were 51.65 MPa, 36.90 psi and 7.22 MPa, respectively. GRAPHICAL ABSTRACT

查看原文本刊更多论文

结合实验室玻璃片的陶瓷砖的制作及性能分析

本文报道了陶瓷玻璃屑对陶瓷砖性能的影响。采用三种不同的烧结温度(11000℃、1150℃、1200℃)制备了5种配方(含硼硅酸盐玻璃片0、3、6、9、12%)的陶瓷陶瓷砖。对其物理、显微组织和力学性能进行了分析。x射线衍射分析确保样品中存在不同的结晶相。形态分析也证实了XRD分析的结果。然而，试样的密度在其工作参数内增加。在瓦片中加入玻璃屑提高了烧结过程的动力学，从而降低了开孔率。在1200℃下烧结的试样吸水率保持在公差范围内(~ 0.5%)。在含12%玻璃屑的样品中，观察到最低的吸水值(~ 0.10%)和最高的线性收缩率(~ 8.9%)。此外，与其他合成样品相比，12%玻璃屑的使用使其力学性能得到改善，抗压强度、冲击强度和硬度分别为51.65 MPa、36.90 psi和7.22 MPa。图形抽象

本文章由计算机程序翻译，如有差异，请以英文原文为准。

求助全文

约1分钟内获得全文求助全文

来源期刊

Transactions of the Indian Ceramic Society 工程技术-材料科学：硅酸盐

CiteScore

2.40

自引率

8.30%

发文量

审稿时长

2.3 months

期刊介绍： Transactions of the Indian Ceramic Society is a quarterly Journal devoted to current scientific research, technology and industry-related news on glass and ceramics. The Journal covers subjects such as the chemical, mechanical, optical, electronic and spectroscopic properties of glass and ceramics, and characterization of materials belonging to this family. The Editor invites original research papers, topical reviews, opinions and achievements, as well as industry profiles for publication. The contributions should be accompanied by abstracts, keywords and other details, as outlined in the Instructions for Authors section. News, views and other comments on activities of specific industries and organizations, and also analyses of industrial scenarios are also welcome.

文献相关原料

公司名称	产品信息	采购帮参考价格