Dry sliding wear behaviour of steel (AISI 1078) after coating with steam treatment and manganese phosphating

IF 1.6 Q4 MATERIALS SCIENCE, COATINGS & FILMS
Siddhant Kaushik, Ranvir Singh Panwar
{"title":"Dry sliding wear behaviour of steel (AISI 1078) after coating with steam treatment and manganese phosphating","authors":"Siddhant Kaushik, Ranvir Singh Panwar","doi":"10.1080/17515831.2021.1872931","DOIUrl":null,"url":null,"abstract":"ABSTRACT Coating on a connecting rod of steel (AISI 1078) may be used to reduce the friction and improve the wear resistance to enhance the durability. In this study, the tribological behaviour of uncoated, steam-coated and manganese phosphate-coated steel (AISI 1078) specimens was investigated. Wear tests were carried out by using a pin on disc apparatus operating at a constant velocity of 1.6 m/s under the normal load from 9.8 to 49 N at room temperature. Increment in wear rate was observed by increasing the applied load. However, steam-coated specimen shows better wear resistance than all other specimens at both low and high loads. For a better understanding of the involved wear mechanism, worn surfaces and collected debris were analysed under a scanning electron microscope, which point out that both adhesive and abrasive mechanism were involved during wear testing of specimens. GRAPHICAL ABSTRACT","PeriodicalId":23331,"journal":{"name":"Tribology - Materials, Surfaces & Interfaces","volume":"15 1","pages":"292 - 302"},"PeriodicalIF":1.6000,"publicationDate":"2021-01-27","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://sci-hub-pdf.com/10.1080/17515831.2021.1872931","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Tribology - Materials, Surfaces & Interfaces","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1080/17515831.2021.1872931","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, COATINGS & FILMS","Score":null,"Total":0}
引用次数: 0

Abstract

ABSTRACT Coating on a connecting rod of steel (AISI 1078) may be used to reduce the friction and improve the wear resistance to enhance the durability. In this study, the tribological behaviour of uncoated, steam-coated and manganese phosphate-coated steel (AISI 1078) specimens was investigated. Wear tests were carried out by using a pin on disc apparatus operating at a constant velocity of 1.6 m/s under the normal load from 9.8 to 49 N at room temperature. Increment in wear rate was observed by increasing the applied load. However, steam-coated specimen shows better wear resistance than all other specimens at both low and high loads. For a better understanding of the involved wear mechanism, worn surfaces and collected debris were analysed under a scanning electron microscope, which point out that both adhesive and abrasive mechanism were involved during wear testing of specimens. GRAPHICAL ABSTRACT
钢(AISI 1078)在蒸汽处理和锰磷化涂层后的干滑动磨损行为
钢(AISI 1078)连杆上的涂层可用于减少摩擦,提高耐磨性,以提高耐久性。在本研究中,研究了未涂层、蒸汽涂层和磷酸锰涂层钢(AISI 1078)试样的摩擦学行为。磨损试验是通过使用以1.6的恒定速度运行的销-盘装置进行的 在9.8至49的正常负载下m/s 室温下为N。通过增加施加的载荷,观察到磨损率的增加。然而,蒸汽涂层试样在低载荷和高载荷下都比所有其他试样表现出更好的耐磨性。为了更好地了解所涉及的磨损机制,在扫描电子显微镜下对磨损表面和收集的碎屑进行了分析,指出在试样的磨损测试过程中,既涉及粘合机制,也涉及研磨机制。图形摘要
本文章由计算机程序翻译,如有差异,请以英文原文为准。
求助全文
约1分钟内获得全文 求助全文
来源期刊
Tribology - Materials, Surfaces & Interfaces
Tribology - Materials, Surfaces & Interfaces MATERIALS SCIENCE, COATINGS & FILMS-
CiteScore
2.80
自引率
0.00%
发文量
15
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信