Effect of water absorption on the Weibull distribution of fatigue test in jute-reinforced polyester composite materials

Abstract

Composite materials have been manufactured using bidirectional jute yarn in a polyester matrix. The manufactured composite has been subjected to water aging for various times of immersion (90, 180, and 270 days). A significant decrease of fatigue strength has been observed during water aging. The number of cycles to failure of the aged and nonaged specimens were correlated using the two-parameter Weibull distribution function to determine the probability of failure and plot the S–N curves at different reliability levels. The results have shown that the two-parameter Weibull distribution describes the fatigue life probability distributions of jute-reinforced polyester composite material with highly significant statistical correlation coefficients.