Study on nanocrystalline coating prepared by electro-spraying 316L metal wire and its corrosion performance

Abstract

Abstract In this work, we study the corrosion performance of coatings prepared by electrical explosion spraying of metal wires. 316L metal wire with a diameter of 1.5 mm is used as spray material, and the coating is prepared on the 45# steel substrate by electrical explosion spraying. The oil–water corrosion experiment of the coating is carried out in a constant temperature water bath of 60°C for 168 h. The scanning electron microscopy and energy-dispersive spectroscopy results of the experimental samples have shown that some metal oxides are found inside the coating, most of which are distributed at the grain boundaries with a size range of 30–50 nm. The corrosion rate of the coating is measured by weight loss method with a corrosion rate of 0.079 mm/annum. XRD results show that the corrosion generates CaCO3, Fe3O4, and MgFe2O4. Coating corrosion is mainly caused by the formation of electrochemical corrosion between oxides and non-oxides in the coating, and pitting corrosion and intergranular corrosion in the presence of chloride ions.