[Studies on sintering of dental porcelain. (Part 1) Binary system sintering of alumina and low fusing frit (author's transl)].

Abstract

Dental porcelains were made from frit and glass powder with electro fused alumina powder addition in the range from 20 to 60 wt% using sintering method at the temperature from 500 degree C to 1 000 degree C, and the effects of alumina content and firing temperature on firing processes of sintered composite were investigated. Shrinkage curves of the powder compacts varied with kind of frit and content of alumina. Particulary, powder compact with alumina addition in the range from 50 to 55% was found to have a remarkable influence for extention of firing temperature range. The densification of the powder compacts was considered to be accelerated by the dissolution of a small a mount of alumina particle into the frit and glass above 900 degree C. Expansion coefficient value of sintered composite of alumina and Pyrex glass powder gradually increased with increase of alumina content. Inversely, expansion coefficient of soda-lime-silica glass showed the minimum value at 40 wt% alumina content and then had a tendency of slight increases with increase of alumina content.