Haijiang Zhang, Shanhua Xu, Jun Li, Anbang Li, Lihua Zhu
{"title":"Effects of Pitting Corrosion on the Void Deformation in Crack Tip Region","authors":"Haijiang Zhang, Shanhua Xu, Jun Li, Anbang Li, Lihua Zhu","doi":"10.1007/s13296-025-01002-1","DOIUrl":null,"url":null,"abstract":"<div><p>Corrosion will reduce the threshold for the expansion of existing cracks in steel structures. To establish the criterion for the propagation of existing cracks in corroded steel structures, it is necessary to study the microscopic mechanism of ductile fracture in the crack tip area of corroded steel plate. This paper aimed to investigate the void deformation characteristic in the crack tip region of corroded steel plates based on computational cubic cell models. By setting boundary constraint, the computational cell models considering the crack tip stress states with pit effects could be established. The pit did not change the evolution modes of the crack tip microscopic void, but the pit depth and shape had influence on the closing speed and degree of the micro-voids in the crack tip steel. The fracture initiation criterion of corroded cracked steel plates could be established based on the micro void evolution mechanism in the crack tip region considering pit effects.</p></div>","PeriodicalId":596,"journal":{"name":"International Journal of Steel Structures","volume":"25 5","pages":"1071 - 1083"},"PeriodicalIF":1.3000,"publicationDate":"2025-10-03","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"International Journal of Steel Structures","FirstCategoryId":"5","ListUrlMain":"https://link.springer.com/article/10.1007/s13296-025-01002-1","RegionNum":4,"RegionCategory":"工程技术","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"CONSTRUCTION & BUILDING TECHNOLOGY","Score":null,"Total":0}
引用次数: 0
Abstract
Corrosion will reduce the threshold for the expansion of existing cracks in steel structures. To establish the criterion for the propagation of existing cracks in corroded steel structures, it is necessary to study the microscopic mechanism of ductile fracture in the crack tip area of corroded steel plate. This paper aimed to investigate the void deformation characteristic in the crack tip region of corroded steel plates based on computational cubic cell models. By setting boundary constraint, the computational cell models considering the crack tip stress states with pit effects could be established. The pit did not change the evolution modes of the crack tip microscopic void, but the pit depth and shape had influence on the closing speed and degree of the micro-voids in the crack tip steel. The fracture initiation criterion of corroded cracked steel plates could be established based on the micro void evolution mechanism in the crack tip region considering pit effects.
期刊介绍：
The International Journal of Steel Structures provides an international forum for a broad classification of technical papers in steel structural research and its applications. The journal aims to reach not only researchers, but also practicing engineers. Coverage encompasses such topics as stability, fatigue, non-linear behavior, dynamics, reliability, fire, design codes, computer-aided analysis and design, optimization, expert systems, connections, fabrications, maintenance, bridges, off-shore structures, jetties, stadiums, transmission towers, marine vessels, storage tanks, pressure vessels, aerospace, and pipelines and more.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号