{"title":"Wear Behavior of TiN/TiAlSiN Nanocomposite Multilayer Coatings from Ambient Temperature to Medium Temperature","authors":"Hairui Ma, Qiang Miao, Wenping Liang, Shijie Sun, Yan Qi, Feilong Jia, Xiangle Chang","doi":"10.3390/coatings14091139","DOIUrl":null,"url":null,"abstract":"TiN/TiAlSiN nanocomposite multilayer coatings were deposited on a titanium alloy by multi-arc ion plating. The investigation of the wear behavior of TiN/TiAlSiN multilayer coatings against Si3N4 was conducted at temperatures of 25 °C, 300 °C, and 500 °C using a ball-on-disk tribometer. Additionally, to gain a deeper understanding of medium-temperature oxidation products, an oxidation test was performed at 500 °C for 10 h. The microstructure and chemical composition of the coatings were evaluated by X-ray diffraction and scanning electron microscopy. The primary peak in the XRD pattern of the multilayer coating changed from TiN (111) to Ti3AlN (111) after the oxidation test. The hardness of the TiN/TiAlSiN multilayer coating was 1540 HV0.1, representing a notable five times improvement compared to the substrate. The critical load in the scratch test was 52.3 N, indicating robust adhesion performance. The wear rate exhibited a sharp increase from 25 °C to 300 °C, compared to the rise from 300 °C to 500 °C. Furthermore, the friction coefficient of the coated sample was more stable than the substrate, with different scratch track morphologies between the samples before and after the oxidation test.","PeriodicalId":10520,"journal":{"name":"Coatings","volume":null,"pages":null},"PeriodicalIF":2.9000,"publicationDate":"2024-09-04","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Coatings","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.3390/coatings14091139","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"MATERIALS SCIENCE, COATINGS & FILMS","Score":null,"Total":0}
引用次数: 0
Abstract
TiN/TiAlSiN nanocomposite multilayer coatings were deposited on a titanium alloy by multi-arc ion plating. The investigation of the wear behavior of TiN/TiAlSiN multilayer coatings against Si3N4 was conducted at temperatures of 25 °C, 300 °C, and 500 °C using a ball-on-disk tribometer. Additionally, to gain a deeper understanding of medium-temperature oxidation products, an oxidation test was performed at 500 °C for 10 h. The microstructure and chemical composition of the coatings were evaluated by X-ray diffraction and scanning electron microscopy. The primary peak in the XRD pattern of the multilayer coating changed from TiN (111) to Ti3AlN (111) after the oxidation test. The hardness of the TiN/TiAlSiN multilayer coating was 1540 HV0.1, representing a notable five times improvement compared to the substrate. The critical load in the scratch test was 52.3 N, indicating robust adhesion performance. The wear rate exhibited a sharp increase from 25 °C to 300 °C, compared to the rise from 300 °C to 500 °C. Furthermore, the friction coefficient of the coated sample was more stable than the substrate, with different scratch track morphologies between the samples before and after the oxidation test.
CoatingsMaterials Science-Surfaces, Coatings and Films
CiteScore
5.00
自引率
11.80%
发文量
1657
审稿时长
1.4 months
期刊介绍:
Coatings is an international, peer-reviewed open access journal of coatings and surface engineering. It publishes reviews, research articles, communications and technical notes. Our aim is to encourage scientists to publish their experimental and theoretical results in as much detail as possible. There is no restriction on the length of the papers. Full experimental and/or methodical details must be provided. There are, in addition, unique features of this journal:
* manuscripts regarding research proposals and research ideas will be particularly welcomed
* electronic files or software regarding the full details of the calculation and experimental procedure - if unable to be published in a normal way - can be deposited as supplementary material