O. T. Tsyrulnyk, O. Z. Student, O. I. Zvirko, D. O. Demianchuk, O. I. Venhryniuk
{"title":"Assessment of Hydrogen Embrittlement of Operated Pipe Steel Using the J-Integral Method","authors":"O. T. Tsyrulnyk, O. Z. Student, O. I. Zvirko, D. O. Demianchuk, O. I. Venhryniuk","doi":"10.1007/s11003-024-00830-6","DOIUrl":null,"url":null,"abstract":"<p>Fracture due to hydrogen embrittlement is a major concern for the reliability and safety of hydrogen transportation via gas pipelines. Pipe steels are characterized by high plasticity, therefore, methods of nonlinear fracture mechanics, including the <i>J</i>-integral method, are preferred for determining the fracture toughness. The influence of preliminary electrochemical hydrogen charging under a moderate mode on fracture toughness of API 5L X67 steel in the as-delivered and 34-year operated on the gas main pipeline conditions was studied. A methodological feature of the experiments is the use of different rates of mechanical loading of specimens with cracks. The influence of the long-term operation of steel on its resistance to brittle fracture is revealed, depending on the test conditions.</p>","PeriodicalId":18230,"journal":{"name":"Materials Science","volume":"10 1","pages":""},"PeriodicalIF":0.7000,"publicationDate":"2024-08-13","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Science","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1007/s11003-024-00830-6","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
Fracture due to hydrogen embrittlement is a major concern for the reliability and safety of hydrogen transportation via gas pipelines. Pipe steels are characterized by high plasticity, therefore, methods of nonlinear fracture mechanics, including the J-integral method, are preferred for determining the fracture toughness. The influence of preliminary electrochemical hydrogen charging under a moderate mode on fracture toughness of API 5L X67 steel in the as-delivered and 34-year operated on the gas main pipeline conditions was studied. A methodological feature of the experiments is the use of different rates of mechanical loading of specimens with cracks. The influence of the long-term operation of steel on its resistance to brittle fracture is revealed, depending on the test conditions.
期刊介绍：
Materials Science reports on current research into such problems as cracking, fatigue and fracture, especially in active environments as well as corrosion and anticorrosion protection of structural metallic and polymer materials, and the development of new materials.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号