Jinliang Chen , Qi Lai , Xiguang Zhao , Jianhong Yi , Qiang Li
{"title":"Effect of room temperature rolling and annealing on microstructure and mechanical properties of (CrCoNi)96V4 medium entropy alloy","authors":"Jinliang Chen , Qi Lai , Xiguang Zhao , Jianhong Yi , Qiang Li","doi":"10.1016/j.intermet.2024.108468","DOIUrl":null,"url":null,"abstract":"<div><p>As cast (CrCoNi)<sub>96</sub>V<sub>4</sub> medium entropy alloy（MEA）was prepared by vacuum arc melting. The MEA is deformed by rolling at room temperature with a total deformation of 67 %, The yield strength and tensile strength of the deformed MEA are 1297 MPa and 1410 MPa respectively, the elongation of the alloy is only 8 %.Then the deformed MEA was annealed for 30min at 700 °C, 800 °C and 900 °C respectively. The results show that the strength and ductility of the MEA after annealing were well balanced. The yield strength and tensile strength of the MEA after annealing at 900 °C/30 min are 678 MPa and 1024 MPa, and the elongation is maintained at 26 %. After annealing, a large number of annealing twins were formed in the MEA, which makes the strength and ductility of the MEA significantly improved. At the same time, Cr-rich particles were found in the MEA, which had positive effect on the improvement of the strength and ductility of the alloy.</p></div>","PeriodicalId":331,"journal":{"name":"Intermetallics","volume":"174 ","pages":"Article 108468"},"PeriodicalIF":4.3000,"publicationDate":"2024-08-29","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Intermetallics","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S0966979524002875","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"CHEMISTRY, PHYSICAL","Score":null,"Total":0}
引用次数: 0
Abstract
As cast (CrCoNi)96V4 medium entropy alloy（MEA）was prepared by vacuum arc melting. The MEA is deformed by rolling at room temperature with a total deformation of 67 %, The yield strength and tensile strength of the deformed MEA are 1297 MPa and 1410 MPa respectively, the elongation of the alloy is only 8 %.Then the deformed MEA was annealed for 30min at 700 °C, 800 °C and 900 °C respectively. The results show that the strength and ductility of the MEA after annealing were well balanced. The yield strength and tensile strength of the MEA after annealing at 900 °C/30 min are 678 MPa and 1024 MPa, and the elongation is maintained at 26 %. After annealing, a large number of annealing twins were formed in the MEA, which makes the strength and ductility of the MEA significantly improved. At the same time, Cr-rich particles were found in the MEA, which had positive effect on the improvement of the strength and ductility of the alloy.
期刊介绍：
This journal is a platform for publishing innovative research and overviews for advancing our understanding of the structure, property, and functionality of complex metallic alloys, including intermetallics, metallic glasses, and high entropy alloys.
The journal reports the science and engineering of metallic materials in the following aspects:
Theories and experiments which address the relationship between property and structure in all length scales.
Physical modeling and numerical simulations which provide a comprehensive understanding of experimental observations.
Stimulated methodologies to characterize the structure and chemistry of materials that correlate the properties.
Technological applications resulting from the understanding of property-structure relationship in materials.
Novel and cutting-edge results warranting rapid communication.
The journal also publishes special issues on selected topics and overviews by invitation only.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号