{"title":"Friction weldability of ultrafine-grained titanium grade 2","authors":"","doi":"10.1016/j.jajp.2024.100246","DOIUrl":null,"url":null,"abstract":"<div><p>The paper presents the results of an experimental study of the friction weldability of Titanium Grade 2 with ultrafine-grained (UFG) microstructure obtained by hydrostatic extrusion and rotary swaging (HE+RS). High-speed friction welding with different rotational speed (<em>n</em>) values was used as a joining method. The best properties were obtained for <em>n</em>=7000 rpm. Metallographic observations confirmed the formation of a continuous friction joint with a changed microstructure of the base material in the thermal-mechanical affected zone (TMAZ) and a friction weld (FW). The results of the mechanical properties showed the greatest decrease in hardness in the TMAZ. The friction welded joint had an 18 % lower tensile strength value than initial state UFG Titanium Grade 2 after the HE+RS process (with UTS=1050 MPa).</p></div>","PeriodicalId":34313,"journal":{"name":"Journal of Advanced Joining Processes","volume":null,"pages":null},"PeriodicalIF":3.8000,"publicationDate":"2024-08-26","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S2666330924000621/pdfft?md5=b28c8deec0f62e706bc0fd10cfcaed21&pid=1-s2.0-S2666330924000621-main.pdf","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Advanced Joining Processes","FirstCategoryId":"1085","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2666330924000621","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0
Abstract
The paper presents the results of an experimental study of the friction weldability of Titanium Grade 2 with ultrafine-grained (UFG) microstructure obtained by hydrostatic extrusion and rotary swaging (HE+RS). High-speed friction welding with different rotational speed (n) values was used as a joining method. The best properties were obtained for n=7000 rpm. Metallographic observations confirmed the formation of a continuous friction joint with a changed microstructure of the base material in the thermal-mechanical affected zone (TMAZ) and a friction weld (FW). The results of the mechanical properties showed the greatest decrease in hardness in the TMAZ. The friction welded joint had an 18 % lower tensile strength value than initial state UFG Titanium Grade 2 after the HE+RS process (with UTS=1050 MPa).
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号