{"title":"Thick Columnar-Structured Thermal Barrier Coatings Using the Suspension Plasma Spray Process","authors":"Dianying Chen, Christopher Dambra","doi":"10.3390/coatings14080996","DOIUrl":null,"url":null,"abstract":"Higher operating temperatures for gas turbine engines require highly durable thermal barrier coatings (TBCs) with improved insulation properties. A suspension plasma spray process (SPS) had been developed for the deposition of columnar-structured TBCs. SPS columnar TBCs are normally achieved at a short standoff distance (50.0 mm–75.0 mm), which is not practical when coating complex-shaped engine hardware since the plasma torch may collide with the components being sprayed. Therefore, it is critical to develop SPS columnar TBCs at longer standoff distances. In this work, a commercially available pressure-based suspension delivery system was used to deliver the suspension to the plasma jet, and a high-enthalpy TriplexPro-210 plasma torch was used for the SPS coating deposition. Suspension injection pressure was optimized to maximize the number of droplets injected into the hot plasma core and achieving the best particle-melting states and deposition efficiency. The highest deposition efficiency of 51% was achieved at 0.34 MPa injection pressure with a suspension flow rate of 31.0 g/min. With the optimized process parameters, 1000 μm thick columnar-structured SPS 8 wt% Y2O3-stabilized ZrO2 (8YSZ) TBCs were successfully developed at a standoff distance of 100.0 mm. The SPS TBCs have a columnar width between 100 μm and 300 μm with a porosity of ~22%. Furnace cycling tests at 1125 °C showed the SPS columnar TBCs had an average life of 1012 cycles, which is ~2.5 times that of reference air-plasma-sprayed dense vertically cracked TBCs with the same coating thickness. The superior durability of the SPS columnar TBCs can be attributed to the high-strain-tolerant microstructure. SEM cross-section characterization indicated the failure of the SPS TBCs occurred at the ceramic top coat and thermally grown oxide (TGO) interface.","PeriodicalId":10520,"journal":{"name":"Coatings","volume":"26 1","pages":""},"PeriodicalIF":2.9000,"publicationDate":"2024-08-07","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Coatings","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.3390/coatings14080996","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q2","JCRName":"MATERIALS SCIENCE, COATINGS & FILMS","Score":null,"Total":0}
引用次数: 0
Abstract
Higher operating temperatures for gas turbine engines require highly durable thermal barrier coatings (TBCs) with improved insulation properties. A suspension plasma spray process (SPS) had been developed for the deposition of columnar-structured TBCs. SPS columnar TBCs are normally achieved at a short standoff distance (50.0 mm–75.0 mm), which is not practical when coating complex-shaped engine hardware since the plasma torch may collide with the components being sprayed. Therefore, it is critical to develop SPS columnar TBCs at longer standoff distances. In this work, a commercially available pressure-based suspension delivery system was used to deliver the suspension to the plasma jet, and a high-enthalpy TriplexPro-210 plasma torch was used for the SPS coating deposition. Suspension injection pressure was optimized to maximize the number of droplets injected into the hot plasma core and achieving the best particle-melting states and deposition efficiency. The highest deposition efficiency of 51% was achieved at 0.34 MPa injection pressure with a suspension flow rate of 31.0 g/min. With the optimized process parameters, 1000 μm thick columnar-structured SPS 8 wt% Y2O3-stabilized ZrO2 (8YSZ) TBCs were successfully developed at a standoff distance of 100.0 mm. The SPS TBCs have a columnar width between 100 μm and 300 μm with a porosity of ~22%. Furnace cycling tests at 1125 °C showed the SPS columnar TBCs had an average life of 1012 cycles, which is ~2.5 times that of reference air-plasma-sprayed dense vertically cracked TBCs with the same coating thickness. The superior durability of the SPS columnar TBCs can be attributed to the high-strain-tolerant microstructure. SEM cross-section characterization indicated the failure of the SPS TBCs occurred at the ceramic top coat and thermally grown oxide (TGO) interface.
CoatingsMaterials Science-Surfaces, Coatings and Films
CiteScore
5.00
自引率
11.80%
发文量
1657
审稿时长
1.4 months
期刊介绍:
Coatings is an international, peer-reviewed open access journal of coatings and surface engineering. It publishes reviews, research articles, communications and technical notes. Our aim is to encourage scientists to publish their experimental and theoretical results in as much detail as possible. There is no restriction on the length of the papers. Full experimental and/or methodical details must be provided. There are, in addition, unique features of this journal:
* manuscripts regarding research proposals and research ideas will be particularly welcomed
* electronic files or software regarding the full details of the calculation and experimental procedure - if unable to be published in a normal way - can be deposited as supplementary material