{"title":"In situ compressive behavior of carbon fibers reinforced PolyEtherEther Ketone laminates exposed to one-sided heat flux","authors":"Benoit Vieille, Alexis Coppalle","doi":"10.1177/00219983241248754","DOIUrl":null,"url":null,"abstract":"This study investigates the influence of a combined thermal heat flux (imposed by a cone calorimeter) and a compressive loading on the deformation and damage mechanisms within quasi-isotropic carbon fibers reinforced PolyEtherEther Ketone laminates. Thermogravimetric Analyses conducted at increasing heating rates under nitrogen (from 5 to 500°C/min) provide valuable information on the thermal decomposition of C/PEEK that ranges from 550°C to 627°C, with a corresponding mass loss ranging from 20 to 26%. From the thermo-mechanical coupling standpoint, the softening and the thermal decomposition of the PEEK matrix under a 50 kW/m<jats:sup>2</jats:sup> heat flux result in the micro-buckling of fibers bundles in matrix-rich areas at the ply scale. Ultimately, it leads to the formation and propagation in the transverse direction of plastic kink bands at the laminates scale. Post-failure observations show that this macroscopic kinking propagates specifically according to the PEEK matrix pyrolysis.","PeriodicalId":15489,"journal":{"name":"Journal of Composite Materials","volume":null,"pages":null},"PeriodicalIF":2.3000,"publicationDate":"2024-04-16","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Composite Materials","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1177/00219983241248754","RegionNum":3,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"MATERIALS SCIENCE, COMPOSITES","Score":null,"Total":0}
引用次数: 0
Abstract
This study investigates the influence of a combined thermal heat flux (imposed by a cone calorimeter) and a compressive loading on the deformation and damage mechanisms within quasi-isotropic carbon fibers reinforced PolyEtherEther Ketone laminates. Thermogravimetric Analyses conducted at increasing heating rates under nitrogen (from 5 to 500°C/min) provide valuable information on the thermal decomposition of C/PEEK that ranges from 550°C to 627°C, with a corresponding mass loss ranging from 20 to 26%. From the thermo-mechanical coupling standpoint, the softening and the thermal decomposition of the PEEK matrix under a 50 kW/m2 heat flux result in the micro-buckling of fibers bundles in matrix-rich areas at the ply scale. Ultimately, it leads to the formation and propagation in the transverse direction of plastic kink bands at the laminates scale. Post-failure observations show that this macroscopic kinking propagates specifically according to the PEEK matrix pyrolysis.
期刊介绍:
Consistently ranked in the top 10 of the Thomson Scientific JCR, the Journal of Composite Materials publishes peer reviewed, original research papers from internationally renowned composite materials specialists from industry, universities and research organizations, featuring new advances in materials, processing, design, analysis, testing, performance and applications. This journal is a member of the Committee on Publication Ethics (COPE).