Influence of LaMnO3 Nanocrystallite Size on its Optical and Raman Spectra

Abstract

In the current study, nanocrystalline LaMnO3 perovskite was prepared by combustion method and annealed at different annealing temperatures. The X-ray diffraction (XRD) patterns provided evidence that the structure formed has a Rhombohedral structure with R3 ̅c space group. The remarkable growth in the crystallite size, reduction in microstrain, and dislocation density were observed with annealing temperature. Ultraviolet-visible spectroscopy was used to determine the optical band gap by the Tauc-plot method. The optical band gap was found to be 3.5 ± 0.4eV and 2.9 ± 0.5eV for 600°C and 1200°C annealed samples, respectively. The observed results were influenced by crystallite size. Raman spectra of the LaMnO3 nanocrystallites revealed five Raman-active modes, like out-of-phase rotation modes and bending mode of MnO6 octahedra. Moreover, the intensity of vibrational modes also varied significantly with annealing temperature.