Influence of production technology of thick plate rolled from shipbuilding steel of strength level 500 on structure parameters and workability characteristics at low temperatures

Abstract

The influence of manufacturing technology of low-alloy steel with yield strength not less than 500 MPa on structure parameters has been studied. Under industrial conditions, two 50 mm thick sheets were produced by different technologies: 1) hot rolling followed by furnace quenching and high-temperature tempering; 2) quenching from rolling heating followed by high-temperature tempering. By means of optical, scanning and transmission electron microscopy the structural features of steel were revealed. Standard mechanical properties and low-temperature serviceability characteristics were determined.