Fabrication and anti-corrosion performances of robust superhydrophobic surface on NAB via solution-etching

Abstract

A labyrinth microstructure interconnected by micron and submicron acicular structures was successfully prepared by immersing nickel-aluminum bronze in 9 wt% FeCl3·6H2O solution at room temperature for 40 min. After being modified with 1H, 1H, 2H, 2H-perfluorodecyltriethoxysilane (FAS-17), the microstructure surface displays robustly low-adhesion superhydrophobicity, and the water contact angle is above 160 ° on it. In addition, the superhydrophobic surface exhibits excellent corrosion resistance and stability in 3.5wt % NaCl aqueous solution and corrosion solution with different pH values.