V. R. Skalskyi, I. M. Dmytrakh, O. T. Tsyrulnyk, A. M. Syrotyuk, O. I. Zvirko
{"title":"Development of a Method for Controlled Hydrogen Fragmentation of Medium-Carbon Steels to Reduce Their Crack Resistance","authors":"V. R. Skalskyi, I. M. Dmytrakh, O. T. Tsyrulnyk, A. M. Syrotyuk, O. I. Zvirko","doi":"10.1007/s11223-024-00600-4","DOIUrl":null,"url":null,"abstract":"<p>The paper considers the use of hydrogen as a component of the technological process to solve an applied problem - the control of material defects, which consisted of controlled fragmentation of steel under dynamic loading to facilitate the cracking of the metal volume. Medium-carbon pearlite-ferrite steel of steel 60 types under electrochemical hydrogenation is studied. The criterion parameter of the material state was the energy of impact loading by three-point bending of smooth beam specimens. By selecting the electrochemical hydrogenation modes in terms of intensity (current) and duration of the process, as well as the composition of the electrolyte, a significant reduction in the energy intensity of steel fracture was obtained, which correlates with the residual hydrogen concentration in the metal. Metallographic analysis of the surface of the specimens confirmed the hydrogenation effect on the initiation of defects, which can be used for controlled steel fragmentation.</p>","PeriodicalId":22007,"journal":{"name":"Strength of Materials","volume":null,"pages":null},"PeriodicalIF":0.7000,"publicationDate":"2024-02-27","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Strength of Materials","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1007/s11223-024-00600-4","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, CHARACTERIZATION & TESTING","Score":null,"Total":0}
引用次数: 0
Abstract
The paper considers the use of hydrogen as a component of the technological process to solve an applied problem - the control of material defects, which consisted of controlled fragmentation of steel under dynamic loading to facilitate the cracking of the metal volume. Medium-carbon pearlite-ferrite steel of steel 60 types under electrochemical hydrogenation is studied. The criterion parameter of the material state was the energy of impact loading by three-point bending of smooth beam specimens. By selecting the electrochemical hydrogenation modes in terms of intensity (current) and duration of the process, as well as the composition of the electrolyte, a significant reduction in the energy intensity of steel fracture was obtained, which correlates with the residual hydrogen concentration in the metal. Metallographic analysis of the surface of the specimens confirmed the hydrogenation effect on the initiation of defects, which can be used for controlled steel fragmentation.
期刊介绍：
Strength of Materials focuses on the strength of materials and structural components subjected to different types of force and thermal loadings, the limiting strength criteria of structures, and the theory of strength of structures. Consideration is given to actual operating conditions, problems of crack resistance and theories of failure, the theory of oscillations of real mechanical systems, and calculations of the stress-strain state of structural components.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号