Long-Term Stability of Ni-Sn-Fe-Based Coatings Prepared by Electrodeposition for the Oxygen Evolution Reaction

Abstract

A coating comprising Ni, Sn, and Fe was deposited on a Ni mesh by cathodic polarization from a bath containing Ni 2+ , Sn 2+ , and Fe 3+ salts in solution, and the oxygen evolution reaction properties of the thus obtained electrode were investigated. The lattice volume of the Ni–Sn–Fe-based coating was estimated to be 77.1 Å 3 , a much larger value than that (44.0 Å 3 ) of the Ni–Fe-based coating obtained in the absence of Sn 2+ . The Ni–Sn–Fe-coated electrode manufactured by cathodic polarization at a current density of −120 mA cm −2 afforded a current density of 10 mA cm −2 at an overpotential of 276 mV in 1 M KOH. The said electrode’s Tafel slope was estimated to be 37 mV dec −1 . When electrolyzed at constant current density (+50 mA cm −2 to +800 mA cm −2 ), it exhibited a stable potential for at least 162 h. The Ni–Sn–Fe-coated electrode was also used as the anode in a two-electrode cell (80 °C; 30 wt% KOH) and electrolyzed for 3 d. Evidence indicated a low cell voltage of 1.81 V at a current density of +600 mA cm −2 , which is at an industrial level.