Effect of Aging on the Ballistic Performance of AA 7017 Alloy

Abstract

This study presents the effect of aging on microstructure, texture, mechanical and ballistic properties of AA-7017 aluminium alloy. AA-7017 alloy is subjected to three different aging namely under-aging, peak-aging and over-aging. Significant difference is observed in the mechanical properties after aging. The alloy exhibits maximum strength and hardness in the peak-aged condition. From texture measurements, it is noticed that the overall intensity of orientation distribution function increases from under-aged to peak-aged condition. The AA-7017 aged plates are impacted with 7.62 mm steel core projectiles at 820±10 m/s to evaluate the ballistic performance. It is noticed that AA-7017 alloy displays best ballistic resistance in peak-aged condition. Distorted material flow lines and adiabatic shear band induced cracking is detected in post ballistic microstructure. The ballistic performance of AA-7017 alloy is correlated with the variations in the microstructure and mechanical properties with aging