Tribo-corrosion behavior of electroplating, nitrocarburizing, and QPQ processes on barrel finishing

IF 2.4 4区材料科学 Q2 MATERIALS SCIENCE, CHARACTERIZATION & TESTING

Materials Testing Pub Date : 2023-10-19 DOI:10.1515/mt-2023-0056

Aysu Hande Yucel, Alpay Yilmaz, Mustafa Bakkal, Ali Taner Kuzu

引用次数: 0

Abstract

Abstract In this study, the effects of nitrocarburizing, QPQ, and Cr coating on the surface properties of 32CrMoV12-10 gun barrels are discussed. Hardness measurements, pin-on-disc tests, and anodic polarization tests were performed to examine the hardness values, wear resistance, friction coefficient, and corrosion resistance. The hardness of the specimen treated with QPQ was found to be the highest. Comparing the hardness profiles, it was observed that the casing depth of the nitrocarburized sample was shallower than that of the QPQ-treated sample. The pin-on-disc test revealed that the nitrocarburized sample exhibited a high coefficient of friction, while the Cr-coated sample showed the lowest coefficient of friction. Analyzing the Tafel polarization curve, it was determined that the nitrocarburized and QPQ-treated specimens demonstrated similar levels of corrosion resistance. However, it can be noted that the QPQ-treated specimen had a slightly lower corrosion rate.

查看原文本刊更多论文

电镀、氮化碳和QPQ工艺对桶体精加工的摩擦腐蚀行为

摘要本研究探讨了氮碳共渗、QPQ和Cr涂层对32CrMoV12-10枪管表面性能的影响。通过硬度测量、销盘测试和阳极极化测试来检验硬度值、耐磨性、摩擦系数和耐腐蚀性。经QPQ处理后的试样硬度最高。对比硬度分布，发现氮碳处理后的套管深度比qpq处理后的套管深度浅。销盘试验结果表明，氮碳涂层试样的摩擦系数较高，而cr涂层试样的摩擦系数最低。通过对Tafel极化曲线的分析，确定了氮碳处理和qpq处理的试样具有相似的耐蚀性。然而，可以注意到，经过qpq处理的试样具有稍低的腐蚀速率。

本文章由计算机程序翻译，如有差异，请以英文原文为准。

求助全文

约1分钟内获得全文求助全文

来源期刊

Materials Testing 工程技术-材料科学：表征与测试

CiteScore

4.20

自引率

36.00%

发文量

165

审稿时长

4-8 weeks

期刊介绍： Materials Testing is a SCI-listed English language journal dealing with all aspects of material and component testing with a special focus on transfer between laboratory research into industrial application. The journal provides first-hand information on non-destructive, destructive, optical, physical and chemical test procedures. It contains exclusive articles which are peer-reviewed applying respectively high international quality criterions.