Synthesis and Investigation of the Physical Properties of Lead-Free BCZT Ceramics

Abstract

This work presents the structure, microstructure, and physical properties of low sintering temperature lead-free ceramics 0.52(Ba0.7Ca0.3)TiO3-0.48Ba(Zr0.2Ti0.8)O3 doped with nano-sized ZnO particles (noted as BCZT/x, x is the content of ZnO nanoparticles in wt.%, x = 0.00, 0.05, 0.10, 0.15, 0.20, and 0.25). The obtained results of Raman scattering and dielectric measurements have confirmed that Zn2+ has occupied B-site, to cause a deformation in the ABO3-type lattice of the BCZT/x specimens. The 0.15 wt.% ZnO-modified ceramic sintered at 1350°C exhibited excellent piezoelectric parameters: d33 = 420 pC/N, d31 = −174 pC/N, kp = 0.483, kt = 0.423, and k33 = 0.571. The obtained results indicate that the high-quality lead-free BCZT ceramic could be successfully synthesized at a low sintering temperature of 1350°C with an addition of appropriated amount of ZnO nanoparticles. This work also reports the influence of the sintering temperature on structure, microstructure, and piezoelectric properties of BCZT/0.15 compound. By rising sintering temperature, the piezoelectric behaviors were improved and rose up to the best parameters at a sintering temperature of 1450°C (d33 = 576 pC/N and kp = 0.55). The corresponding properties of undoped BCZT ceramics were investigated as a comparison. It also presented that the sintering behavior and piezo-parameters of doped BCZT samples are better than the undoped BCZT samples at each sintering temperature.