HIP for AM - Optimized Material Properties by HIP

Abstract

An investigation of HIP parameters for EBM Ti-6Al-4V has been performed by Arcam AB and Quintus Technologies AB with the aim to maximize the strength of the HIP:ed material. A lower HIP temperature of 800 °C and a higher pressure of 200 MPa gives the highest strength and is also enough to eliminate all internal defects. By printing material with intentionally induced porosity combined with an optimized HIP cycle the highest strength can be obtained. Introduction Hot isostatic pressing (HIP) is widely used today to eliminate internal defects in metallic materials produced by powder bed fusion. The internal defects are mostly lack-of-fusion defects generated during the printing process and entrapped gas porosity coming from the powder particles. These defects act like stress concentrations and crack initiation points in the material, which decreases the material properties. By eliminating these defects within the material, the ductility and especially the fatigue properties are improved [1-5]. Figure 1 shows a cross section of an EBM Ti-6Al-4V material before and after HIP where the typical effect of HIP:ing in terms of defect elimination can be seen. In Figure 2, typical fatigue data of as printed and HIP:ed material of EBM Ti-6Al-4V is shown and it is evident that the HIP process gives much improved fatigue properties compared to as-printed material. This data is generated by Arcam. Figure 1 Micrographs of EBM Ti-6Al-4V before HIP to the left and after HIP to the right Hot Isostatic Pressing – HIP‘17 Materials Research Forum LLC Materials Research Proceedings 10 (2019) 1-10 doi: http://dx.doi.org/10.21741/9781644900031-1 2 Figure 2 Fatigue data for EBM Ti-6Al-4V, courtesy of Arcam The solidification rates in the EBM process are in the order of 10 – 10 K/s which is very high [6]. The extremely fast solidification generates a very fine microstructure which gives the material a high strength. Any conventional heat treatment at an elevated temperature for a significantly long time, like HIP:ing, will coarsen the microstructure due thermodynamic driving forces. This coarsening of the microstructure will decrease the strength of the material, which is not preferable. The development within EBM printing equipment over the last years has made the as-printed microstructures even finer, which makes this challenge even more significant for the modern EBM machines. In Figure 3 a) and b) the microstructure of as printed material compared to HIP:ed EBM Ti-6Al-4V is shown. The coarsening of the microstructure after HIP is evident. Figure 3 a) and c) shows the difference between the microstructures produced by an older Arcam s12 machine compared to a newer Arcam Q10 machine. Figure 3 Microstructures of EBM Ti-6Al-4V a) As-printed with Arcam s12 b) After HIP (920°C, 1000bar, 2h) with Arcam s12 c) As-printed with Arcam Q10 For Ti-6Al-4V produced by selective laser melting (SLM), the same coarsening of the microstructure and thus decrease of strength has been seen. As reported by Leuders [1] the tensile strength of SLM Ti-6Al-4V is decreased by any kind of elevated temperature process including HIP:ing as shown in Figure 4. b c a Hot Isostatic Pressing – HIP‘17 Materials Research Forum LLC Materials Research Proceedings 10 (2019) 1-10 doi: http://dx.doi.org/10.21741/9781644900031-1 3 Figure 4 Tensile test data of SLM Ti-6Al-4V in different conditions [1] The ASTM standard for additive manufactured Ti-6Al-4V by powder bed fusion, F2924-14, specifies a HIP temperature between 895 and 955 °C, a minimum pressure of 100 MPa and a minimum hold time of 2 hours. The widely used HIP parameters for AM Ti-6Al-4V is 920 °C, 100 MPa and 2 hours hold time, thus within the standard specification. However, these HIP parameters were developed for cast Ti-6Al-4V before today’s commercial AM processes existed and it is not obvious that these HIP parameters are optimal for AM material. With this background, a study of HIP parameters for EBM Ti-6Al-4V was made by Arcam and Quintus Technologies with the purpose to evaluate if other HIP parameters could be used to eliminate all defects but have a lower influence on the fine as-printed microstructure. The approach of this study is to evaluate lower HIP temperatures. Experimental The HIP parameter study consisted of 6 different HIP treatments according to Table 1 together with as-printed material as reference. The test specimens for the study were 15 mm diameter rods printed with standard EBM printing parameters and powder and 10 test specimens for each condition were used for the evaluation. Table 1 The 6 different HIP treatments used in the study Variant Temperature [°C] Pressure [MPa] Hold time [hours] Cooling rate [K/min] 1 920 100 2 ~ 30 2 920 100 2 ~ 1500 3 880 100 2 ~ 30 4 840 100 2 ~ 30 5 800 100 2 ~ 30 6 800 200 2 ~ 30 Hot Isostatic Pressing – HIP‘17 Materials Research Forum LLC Materials Research Proceedings 10 (2019) 1-10 doi: http://dx.doi.org/10.21741/9781644900031-1 4 The results of the different HIP variants were evaluated by density, internal defect analysis and tensile data in xy and z-direction. The density was measured by helium pycnometry and with Archimedes principle, here called water intrusion. The internal defects in the material were evaluated by optical microscopy and the tensile data was attained with standard tensile testing. As an extension of the HIP parameter study, material printed with intentional internal porosity was also HIP:ed and analyzed. The intentional induced defects were generated by printing with a larger line off-set up to 0.4 mm instead of the standard 0.2 mm. In Figure 5 the macrostructure of material printed with the standard 0.2 mm line off-set and 0.4 mm line off-set is shown and a large difference in number of defects can be observed. Figure 5 Defects analyzed with LayerQam. To the left with 0.2 mm line off-set and 0.4 mm to the right. Results In Figure 6 the results from the density measurements are presented. As can be seen, all HIP variants gives ~ 100 % density. The material printed with standard parameters also shows ~ 100 % density in the as-printed state. There is still porosity in the material but a relatively small amount as shown in Figure 1 so that no influence is visible in the density measurements. For the material printed with larger line off-set the density is significantly lower than the standard printed material with up to 8 % porosity for the material printed with 0.4 mm line off-set. However, these samples are also fully densified to ~ 100 % density with HIP despite the low starting density. The contour of the porous printed specimens was built with standard printing parameters to achieve a gas tight surface for the specimens. A gas tight outer surface of the part to be HIP:ed is required to ensure full densification by the HIP process without any encapsulation of the part. Hot Isostatic Pressing – HIP‘17 Materials Research Forum LLC Materials Research Proceedings 10 (2019) 1-10 doi: http://dx.doi.org/10.21741/9781644900031-1 5 Figure 6 – Density measurements results The results for the evaluation of defects with optical microscopy showed that HIP variants 1, 2, 3 and 6 gave full defect elimination. HIP variants number 4 and 5 with 840 and 800 °C and 100 MPa showed some small remaining defects which were not eliminated by HIP. The density measurements in Figure 6 also tend to show the same result. The tensile test results for the material printed with standard parameters are shown in Figure 7. The results show that there is a significant increase in strength when going towards lower HIP temperatures. The HIP cycles at 800 °C gives the best strength and the ductility is not influenced significantly by the different HIP variants. Hot Isostatic Pressing – HIP‘17 Materials Research Forum LLC Materials Research Proceedings 10 (2019) 1-10 doi: http://dx.doi.org/10.21741/9781644900031-1