Jurnal Teknik Kimia Indonesia Pub Date : 2018-10-02 DOI:10.5614/jtki.2007.6.2.5

I. Noezar, V. S. Praptowidodo, R. Nugraheni, M. H. Nasution

{"title":"Biodegradable polymer dari asam laktat","authors":"I. Noezar, V. S. Praptowidodo, R. Nugraheni, M. H. Nasution","doi":"10.5614/jtki.2007.6.2.5","DOIUrl":null,"url":null,"abstract":"The objective of this research is to learn and to make the biodegradable polymer, Poly(lactic acid), from lactic acid by condensation polymerization without catalyst. Poly(lactic acid) that will be produced in this research should have the molecular weight between 3000-5000 grams/mole. The scopes of this research are the_purification of lactic acid, purity analysis, polymerization reaction, and polymer's characteristic analysis. The method of lactic acid purification is distillation in nitrogen atmosphere. Polymerization reaction which is used in this research is the condensation polymerization without catalyst. The polymer's characteristics that will be analyzed are molecular weight and degradation time Molecular weight is analyzed by viscosimetry method and Gel Permeation Chromatography. Degradation time is analyzed by landfill method Based on this research, purification of D,L-lactic acid (91%-weight) reaches 98%-weight and for L-lactic acid (93%-weight) reaches 96%-berat. Molecular weight of D,L-lactic acid between 450-3600 grams/mole and L-lactic acid between 4200-8500 grams/mole. The degradation time of polymer is 5 weeks.Keywords: Poly(lactic acid), polymer, biodegradable AbstrakPenelitian ini bertujuan untuk mempelajari dan mensintesis biodegradable polymer, Poly(lactic acid) dari asam laktat melalui reaksi polimerisasi kondensasi tanpa katalis. Poly(lactic acid) yang dihasilkan dalam penelitian ini diharapkan memiliki berat molekul antara 3000-5000 gram/mol. Ruang lingkup penelitian meliputi pemurnian asam laktat, analisa kemurnian asam laktat, reaksi polimerisasi kondensasi dan karakterisasi polimer. Pemurnian asam laktat dilakukan melalui distilasi pada atmosfer nitrogen dan tekanan 1 atmosfer. Reaksi polimerisasi dilakukan melalui polimerisasi kondensasi tanpa katalis dengan variasi waktu reaksi pengadukan mekanik dan laju pemanasan. Karakteristik polimer yang dianalisis adalah berat molekul dan waktu degradasi. Berat molekul dianalisis dengan metode GPC (Gel Permeation Chromatography) dan viskosimetri. Degradasi polimer dilakukan secara landfill. Berdasarkan hasil percobaan, pemurnian asam laktat untuk monomer D,L-Lacticacid (91%-berat) mencapai 98%-berat sedangkan untuk monomer L-Lactic acid (93%-berat) mencapai 96%-berat. Berat molekul yang dihasilkan untuk monomer D,L-Lactic acid adalah 450 - 3600 gram/mol sedangkan untuk monomer L-Lactic acid adalah 4200- 8500 gram/mol. Waktu degradasi polimer secara landfill adalah 5 minggu.Kata kunci : Poly(lactic acid), polimer, biodegradable","PeriodicalId":138501,"journal":{"name":"Jurnal Teknik Kimia Indonesia","volume":"1 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2018-10-02","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"Jurnal Teknik Kimia Indonesia","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.5614/jtki.2007.6.2.5","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

The objective of this research is to learn and to make the biodegradable polymer, Poly(lactic acid), from lactic acid by condensation polymerization without catalyst. Poly(lactic acid) that will be produced in this research should have the molecular weight between 3000-5000 grams/mole. The scopes of this research are the_purification of lactic acid, purity analysis, polymerization reaction, and polymer's characteristic analysis. The method of lactic acid purification is distillation in nitrogen atmosphere. Polymerization reaction which is used in this research is the condensation polymerization without catalyst. The polymer's characteristics that will be analyzed are molecular weight and degradation time Molecular weight is analyzed by viscosimetry method and Gel Permeation Chromatography. Degradation time is analyzed by landfill method Based on this research, purification of D,L-lactic acid (91%-weight) reaches 98%-weight and for L-lactic acid (93%-weight) reaches 96%-berat. Molecular weight of D,L-lactic acid between 450-3600 grams/mole and L-lactic acid between 4200-8500 grams/mole. The degradation time of polymer is 5 weeks.Keywords: Poly(lactic acid), polymer, biodegradable AbstrakPenelitian ini bertujuan untuk mempelajari dan mensintesis biodegradable polymer, Poly(lactic acid) dari asam laktat melalui reaksi polimerisasi kondensasi tanpa katalis. Poly(lactic acid) yang dihasilkan dalam penelitian ini diharapkan memiliki berat molekul antara 3000-5000 gram/mol. Ruang lingkup penelitian meliputi pemurnian asam laktat, analisa kemurnian asam laktat, reaksi polimerisasi kondensasi dan karakterisasi polimer. Pemurnian asam laktat dilakukan melalui distilasi pada atmosfer nitrogen dan tekanan 1 atmosfer. Reaksi polimerisasi dilakukan melalui polimerisasi kondensasi tanpa katalis dengan variasi waktu reaksi pengadukan mekanik dan laju pemanasan. Karakteristik polimer yang dianalisis adalah berat molekul dan waktu degradasi. Berat molekul dianalisis dengan metode GPC (Gel Permeation Chromatography) dan viskosimetri. Degradasi polimer dilakukan secara landfill. Berdasarkan hasil percobaan, pemurnian asam laktat untuk monomer D,L-Lacticacid (91%-berat) mencapai 98%-berat sedangkan untuk monomer L-Lactic acid (93%-berat) mencapai 96%-berat. Berat molekul yang dihasilkan untuk monomer D,L-Lactic acid adalah 450 - 3600 gram/mol sedangkan untuk monomer L-Lactic acid adalah 4200- 8500 gram/mol. Waktu degradasi polimer secara landfill adalah 5 minggu.Kata kunci : Poly(lactic acid), polimer, biodegradable

查看原文本刊更多论文

本研究的目的是学习和制备生物可降解聚合物，聚乳酸，由乳酸缩聚无催化剂。本研究将生产的聚乳酸的分子量应在3000-5000克/摩尔之间。本研究的范围是乳酸的纯化、纯度分析、聚合反应和聚合物的特性分析。乳酸提纯的方法是在氮气气氛中蒸馏。本研究采用的聚合反应是无催化剂的缩聚反应。聚合物的特性是分子量和降解时间。分子量的分析采用粘度法和凝胶渗透色谱法。采用填埋法对降解时间进行了分析。在本研究的基础上，D, l -乳酸(91%重量)的净化达到98%重量，l -乳酸(93%重量)的净化达到96%重量。D, l -乳酸的分子量在450-3600克/摩尔之间，l -乳酸的分子量在4200-8500克/摩尔之间。聚合物降解时间为5周。关键词:聚乳酸，聚合物，可生物降解abstract: penelitian ini bertujuan untuk mempelajari danmensinensis可生物降解聚合物，聚乳酸，dari asam laktat melalui reaksi polerisasi kondensasi tanpa katalis。聚(乳酸)洋迪哈希坎达拉姆penelitian尼迪哈希坎memoriliki berat分子antara 3000-5000克/mol。Ruang lingup penelitian melputi pemurnian asam lakat, analisa kemurnian asam lakat, reaksi polimisasi kondensasi dan karakterisasi polymer。Pemurnian asam laktat dilakukan melalui distilasi pada atmosphere氮和tekanan 1 atmosphere。我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说，我是说。Karakteristik聚合物阳电分析与分子降解的关系。凝胶渗透色谱法(GPC)和粘度计。可降解聚合物的研究。Berdasarkan hasil percobaan, pemurnian asam laktatuntuk单体D, l -乳酸(91%-berat)门限98%-berat sedangkan untuk单体l -乳酸(93%-berat)门限96%-berat。Berat分子yang dihasilkan untuk单体D, l -乳酸adalah 450 - 3600克/mol sedangkan untuk单体l -乳酸adalah 4200- 8500克/mol。Waktu降解聚合物secara填埋adalah 5 minggu。Kata kunci:聚乳酸，聚合物，可生物降解

本文章由计算机程序翻译，如有差异，请以英文原文为准。

求助全文

约1分钟内获得全文求助全文

来源期刊

Jurnal Teknik Kimia Indonesia

自引率

0.00%

发文量