Twin Roll Casting of Copper Alloy C19210 Using Commercial Scale Machine

Abstract

Copper alloy C19210 have excellent corrosion resistance, heat resistance, and conductivity, and is used for precision electronic parts such as lead frame materials. Conventionally, copper alloy strips are manufactured by repeating heat treatment and cold rolling, and have a problem that it is multi-process and production cost is expensive. On the other hand, twin roll casting can improve the above problems because strips are made directly from molten metals. In this study, twin roll strip casting of copper alloy C19210 using commercial scale machine was operated. The aims of this study is to investigate the possibility of strip casting for copper alloy. The effect of the side dam and release agent was researched. The effect of rolls speed on the strip surface condition was researched. The improved side dam prevented molten metal leakage. The release agent prevented sticking of the manufactured strip to the roll surface. The strip produced at roll speed of 7 m/min and 10 m/min had a lot of metallic luster. Moreover, the strip produced at roll speed of 7 m/min had more metallic luster than the strip produced at roll speed of 10 m/min. The lower the roll speed is, the greater the rolling load is. At a roll speed of 7 m / min, the rolling load became the maximum rolling load of the equipment. For producing strips with copper alloy C19210, higher rolling loads are preferred.