Struktur dan Sifat Mekanik Film Bacterial Cellulose dengan Disintegrasi Mekanis

Abstract

Film structure was greatly affected to mechanical properties of Bacterial Cellulose (BC). An engineering effort on Bacterial Cellulose Fibers (BCF) structure was changing the size and distribution of BC fiber through mechanical disintegrator process using a High Speed Blender (HSB). This study aimed to show the effect of disintegrator to the structure and mechanical properties of BCF film. The method used in this study is a synthesis of BCF from fermentation from pineapple peel waste with incubation of Acetobacter xylinum ( A. xylinum ) for 14 days. BC pellicle was soaked by using 1% NaOH for 24 hours then distrusted using the HSB with code speed variation of L (18000 rpm), M (21000 rpm), and H (26000 rpm) for 5 min. Then film formed by a casting method and dried in the oven at a temperature of 60 °C for 8 hours. The study result showed that the morphology of BCF formed pores, the crystallinity decreased so the tensile strength was decreased by 94%. The results of this study are expected to provide engineering information on the BCF structure potentially for filters and for sensors. Struktur film sangat berpengaruh terhadap sifat mekanik dari Bacterial Cellulose (BC). Upaya merekayasa struktur Bacterial Cellulose Fiber s (BCF) adalah dengan mengubah ukuran dan distribusi serat BC melalui proses  disintegrator  mekanis menggunakan High Speed Blender (HSB). Penelitian ini bertujuan untuk mengetahui pengaruh disintegrasi terhadap struktur dan sifat mekanis film BCF. Metode yang digunakan dalam penelitian ini adalah sintesis BCF dari fermentasi limbah kulit nanas dengan inkubasi bakteri Acetobacter xylinum ( A. x ylinum ) selama 14 hari. Serat BC direndam dengan NaOH 1% selama 24 jam kemudian dihaluskan dengan HSB kode variasi kecepatan L (18000 rpm), M (21000 rpm), dan H (26000 rpm) selama 5 menit. Film dibentuk dengan metode casting dan dikeringkan menggunakan oven pada suhu 60 °C selama 8 jam. Hasil penelitian menunjukkan morfologi BCF menjadi berpori dengan kristalinitasnya menurun sehingga kekuatan tarik film juga menurun sebesar 94%. Hasil penelitian ini diharapkan memberikan informasi rekayasa struktur BCF berpotensi untuk filter dan maupun untuk sensor.