Crystallization of vaterite and aragonite on chitin whiskers

Abstract

The need for the possibility of producing calcium carbonate crystals by the evaporation method within five minutes and the growth of different calcium carbonate polymorphs on chitin whiskers within the same time frame at room temperature necessitated these report. Chitin whiskers (CHWs) were used as insoluble substrates, while poly (acrylic) acid (PAA) is used as soluble additive. The crystals were grown in chitin whiskers, Poly (acrylic) acid and CHW/PAA composites. The volume fractions for aragonite, vaterite, and calcite are 0.10, 0.25, and 0.65, respectively, in the absence of chitin whiskers or Poly (acrylic) acid. Calcite and aragonite volume fractions decrease in favour of vaterite when PAA and or CHWs were added. SEM images in the absence of CHWs and PAA shows rhombohedral calcites that display steady and step like plane appearances with an average edge of between 1.3 and 1.4 μm. In the presence of only CHWs, the SEM images show a mixture of ellipsoidal and spherical shape vaterites. The spherical vaterites have smooth, rough, and some irregular surfaces. Rod-like aragonite polymorphs were seen when only PAA was used as the template. In the presence of both PAA and CHWs, the rhombohedral shape showed roughness with irregular faces. Keywords: Chitin whisker, Calcium carbonate, Calcium, vaterite aragonite, Polymorph, Mole fraction