PENGARUH WAKTU CURING TERHADAP KUAT TEKAN GEOPOLIMER BERBASIS FLY ASH

ENSAINS JOURNAL Pub Date : 2019-01-29 DOI:10.31848/ENSAINS.V2I1.152

Andrie Harmaji, Claudia Claudia, Lia A T W Asri, Bambang Sunendar, A. Nuruddin

{"title":"PENGARUH WAKTU CURING TERHADAP KUAT TEKAN GEOPOLIMER BERBASIS FLY ASH","authors":"Andrie Harmaji, Claudia Claudia, Lia A T W Asri, Bambang Sunendar, A. Nuruddin","doi":"10.31848/ENSAINS.V2I1.152","DOIUrl":null,"url":null,"abstract":"Abstract:. Suralaya power plant produces fly ash about 219.000 ton per year. Fly ash contents of silica and alumina as major components that can be used as precursors for geopolymer, a three dimensional networks aluminosilicate polymers. This research aim is to utilize fly ash for geopolymer made by mixing fly ash, fine aggregate, and alkali activator in a cubic mould and curing was carried out at room temperature for 7 and 28 days. After 28 days of curing the compressive strength of geopolymer reached 41.70 MPa. XRD characterization shows Albite (NaAlSi3O8) formation which has similarity to geopolymer compound. Fourier Transform Infra Red spectra show siloxo and sialate bond. These are typical functional groups that are found in geopolymer materials.Keyword: geopolymer, fly ash, aluminosilicate, alkali activator, albite, siloxo, sialateAbstrak: Pembangkit Listrik Tenaga Uap (PLTU) Suralaya menghasilkan fly ash (abu terbang) sekitar 219.000 ton per tahun. Fly ash memiliki silika dan alumina sebagai komponen utama yang dapat digunakan sebagai prekursor untuk geopolimer, suatu material polimer aluminosilikat tiga dimensi. Penelitian ini bertujuan untuk memanfaatkan fly ash untuk geopolimer yang dibuat dengan mencampur fly ash, agregat halus, dan aktivator alkali dalam cetakan kubik dan pengawetan dilakukan pada suhu kamar selama 7 dan 28 hari. Setelah 28 hari curing kekuatan tekan geopolimer mencapai 41,70 MPa. Karakterisasi XRD menunjukkan pembentukan Albite (NaAlSi3O8) yang memiliki kemiripan dengan senyawa geopolimer. Hasil spektroskopi Fourier Transform Infra Red (FTIR) menunjukkan ikatan siloxo dan sialate yang merupakan gugus fungsional khas yang ditemukan dalam geopolimer.Kata Kunci: geopolimer, abu terbang, aluminosilikat, alkali aktivator, albite, siloxo, sialate","PeriodicalId":297097,"journal":{"name":"ENSAINS JOURNAL","volume":"20 1","pages":"0"},"PeriodicalIF":0.0000,"publicationDate":"2019-01-29","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":null,"platform":"Semanticscholar","paperid":null,"PeriodicalName":"ENSAINS JOURNAL","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.31848/ENSAINS.V2I1.152","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}

引用次数: 0

Abstract

Abstract:. Suralaya power plant produces fly ash about 219.000 ton per year. Fly ash contents of silica and alumina as major components that can be used as precursors for geopolymer, a three dimensional networks aluminosilicate polymers. This research aim is to utilize fly ash for geopolymer made by mixing fly ash, fine aggregate, and alkali activator in a cubic mould and curing was carried out at room temperature for 7 and 28 days. After 28 days of curing the compressive strength of geopolymer reached 41.70 MPa. XRD characterization shows Albite (NaAlSi3O8) formation which has similarity to geopolymer compound. Fourier Transform Infra Red spectra show siloxo and sialate bond. These are typical functional groups that are found in geopolymer materials.Keyword: geopolymer, fly ash, aluminosilicate, alkali activator, albite, siloxo, sialateAbstrak: Pembangkit Listrik Tenaga Uap (PLTU) Suralaya menghasilkan fly ash (abu terbang) sekitar 219.000 ton per tahun. Fly ash memiliki silika dan alumina sebagai komponen utama yang dapat digunakan sebagai prekursor untuk geopolimer, suatu material polimer aluminosilikat tiga dimensi. Penelitian ini bertujuan untuk memanfaatkan fly ash untuk geopolimer yang dibuat dengan mencampur fly ash, agregat halus, dan aktivator alkali dalam cetakan kubik dan pengawetan dilakukan pada suhu kamar selama 7 dan 28 hari. Setelah 28 hari curing kekuatan tekan geopolimer mencapai 41,70 MPa. Karakterisasi XRD menunjukkan pembentukan Albite (NaAlSi3O8) yang memiliki kemiripan dengan senyawa geopolimer. Hasil spektroskopi Fourier Transform Infra Red (FTIR) menunjukkan ikatan siloxo dan sialate yang merupakan gugus fungsional khas yang ditemukan dalam geopolimer.Kata Kunci: geopolimer, abu terbang, aluminosilikat, alkali aktivator, albite, siloxo, sialate

查看原文本刊更多论文

CURING时间对压缩以飞灰为基础的地质聚合物的影响

文摘:。苏拉拉亚电厂每年生产约219.9万吨粉煤灰。粉煤灰以二氧化硅和氧化铝为主要成分，可作为地聚合物的前驱体，是一种三维网状的铝硅酸盐聚合物。本研究的目的是利用粉煤灰制备地聚合物，将粉煤灰、细骨料和碱活化剂在立方模中混合，在室温下养护7天和28天。固化28 d后，地聚合物抗压强度达到41.70 MPa。XRD表征表明，钠长石(NaAlSi3O8)的形成与地聚合物相似。傅里叶变换红外光谱显示硅氧烷和硅酸盐键。这些是在地聚合物材料中发现的典型官能团。摘要:Pembangkit Listrik Tenaga Uap (PLTU) Suralaya menghasilkan粉煤灰(abu terbang) sekitar 219.000吨/塔hun。粉煤灰硅酸铝和氧化铝硅酸铝的前驱物硅酸铝的土聚物，水聚材料聚合物硅酸铝的尺寸。Penelitian ini bertujuan untuk memanfaatkan粉煤灰untuk geoolimer yang dibuat dengan mencampur粉煤灰，集料halus, dan活化剂碱dalam cetakan kubik dan pengawetan dilakukan pada suhu kamar selama 7 dan 28 hari。Setelah 28hari固化kekuatan tekan地质聚合物的压力为41,70 MPa。Karakterisasi XRD menunjukkan pembentukan钠长石(NaAlSi3O8) yang memiliki kemiripan dengan senyawa地质聚合物。傅立叶变换红外光谱(FTIR) menunjukkan ikatan siloxo dansialate yang merupakan gugus真菌khas yang ditemukan dalam地质聚合物。卡塔昆奇:地高聚物、硅藻土、硅藻土铝、碱活化剂、钠长石、硅藻土、硅酸盐