Use of Electron Fractography to Diagnose Cracking in a 7075-T6 Aluminum Forging

Abstract

A forging of 7075-T6 aluminum alloy, which formed a support for the cylinder of a cargo door, cracked at an attachment hole. Fluorescent penetrant inspection showed the crack ran above and below the hole out onto the machined flat surface of the flange. A 6500x electron fractograph proved the crack to be a forging defect called a cold shut. Because defects of this type are usually detected when the raw forging is inspected, this occurrence was considered to be an isolated instance.