Effect of incorporating silica-hydroxyapatite-silver hybrid nanoparticles into the resin-modified glass ionomer on the adhesive remnant index score and shear bond strength of orthodontic metal brackets: An in vitro study

Objectives

This study aimed to assess the effect of addition of silica-hydroxyapatite-silver (Si-HA-Ag) hybrid nanoparticles to light-cure glass ionomer (GI) on shear bond strength (SBS) of metal brackets bonded with this adhesive and the adhesive remnant index (ARI) score.

Material and methods

In this in vitro experimental study, 50 sound extracted premolars were assigned to 5 groups (n = 10) for orthodontic metal bracket bonding with BracePaste® composite, Fuji ORTHO™ pure resin modified GI (RMGI), and RMGI reinforced with 2wt%, 5wt% and 10wt% Si-HA-Ag nanoparticles. The SBS of brackets was measured by a universal testing machine. Debonded specimens were inspected under a stereomicroscope at × 10 magnification to determine the ARI score. Data were analyzed by one-way ANOVA, Scheffe test, Chi-square test, and Fisher's exact test (alpha = 0.05).

Results

The maximum mean SBS was recorded in BracePaste® composite followed by 2% RMGI, 0% RMGI, 5% RMGI and 10% RMGI. Only the difference between the BracePaste® composite and 10% RMGI was significant in this regard (P = 0.006). The groups were not significantly different regarding the ARI scores (P = 0.665). All the SBS values were within the clinically acceptable range.

Conclusion

Addition of 2wt% and 5wt% Si-HA-Ag hybrid nanoparticles to RMGI as orthodontic adhesive caused no significant change in SBS of orthodontic metal brackets while addition of 10wt% hybrid nanoparticles significantly decreased the SBS. Nonetheless, all the SBS values were within the clinically acceptable range. Addition of hybrid nanoparticles had no significant effect on the ARI score.