Amal Abdelsamad Sakrana, Ahmed Laith, Ahmed Elsherbini, Fatma Abdallah Elerian, Mutlu Özcan, Walid Al-Zordk
{"title":"树脂胶结物在粘接二硅酸锂和氧化锆修复体时对颜色稳定性的影响。分光光度法研究","authors":"Amal Abdelsamad Sakrana, Ahmed Laith, Ahmed Elsherbini, Fatma Abdallah Elerian, Mutlu Özcan, Walid Al-Zordk","doi":"","DOIUrl":null,"url":null,"abstract":"<p><strong>Aim: </strong>To evaluate the influence of resin cement on the color stability of lithium disilicate and zirconia restorations immersed in coffee after aging.</p><p><strong>Materials and methods: </strong>Eighty maxillary premolars were classified into eight groups (n = 10) based on restorative material type (lithium disilicate or zirconia), resin cement type (G-CEM LinkForce; GC Corporation or Panavia SA Cement Plus Automix; Kuraray Noritake Dental), and preheating temperature (25°C or 54°C). Following tooth preparation, each restoration was bonded to its corresponding substrate. Using a reflectance spectrophotometer, Commission Internationale de l'Éclairage (CIE) tristimulus values were detected and calculated (D65 standard illumination, 10-degree observer angle). All specimens were aged (240,000 load cycles followed by 10,000 thermal cycles), then immersed in coffee (18 h). Following that, the second measurements of the color coordinates were determined. The total color differences were measured, and the data were statistically analyzed (α = 0.05).</p><p><strong>Results: </strong>The temperature had a significant effect on ΔL΄ (P < 0.001), ΔC΄ (P < 0.001), and ΔH΄ (P < 0.001). The lithium disilicate restorations were more color stable than the zirconia restorations. Also, there was a significant difference (P = 0.047) between the LinkForce (2.28 ± 0.48) and Panavia SA (2.15 ± 0.46) cement. The restorations cemented at a temperature of 54°C (1.76 ± 0.11) showed significant color differences (P < 0.001) compared with those cemented at a temperature of 25°C (2.67 ± 0.15). A three-way analysis of variance (ANOVA) test revealed that the interaction between the ceramic material, cement type, and temperature had no statistically significant effect (P = 0.611) on the color stability of the ceramic restorations.</p><p><strong>Conclusions: </strong>Cement type has a significant effect on the color stability of lithium disilicate and zirconia restorations. Cement at a temperature of up to 54°C enhances the color stability of lithium disilicate and zirconia restorations.</p>","PeriodicalId":0,"journal":{"name":"","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-05-11","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Influence of resin cement on color stability when luting lithium disilicate and zirconia restorations. A spectrophotometry study\",\"authors\":\"Amal Abdelsamad Sakrana, Ahmed Laith, Ahmed Elsherbini, Fatma Abdallah Elerian, Mutlu Özcan, Walid Al-Zordk\",\"doi\":\"\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<p><strong>Aim: </strong>To evaluate the influence of resin cement on the color stability of lithium disilicate and zirconia restorations immersed in coffee after aging.</p><p><strong>Materials and methods: </strong>Eighty maxillary premolars were classified into eight groups (n = 10) based on restorative material type (lithium disilicate or zirconia), resin cement type (G-CEM LinkForce; GC Corporation or Panavia SA Cement Plus Automix; Kuraray Noritake Dental), and preheating temperature (25°C or 54°C). Following tooth preparation, each restoration was bonded to its corresponding substrate. Using a reflectance spectrophotometer, Commission Internationale de l'Éclairage (CIE) tristimulus values were detected and calculated (D65 standard illumination, 10-degree observer angle). All specimens were aged (240,000 load cycles followed by 10,000 thermal cycles), then immersed in coffee (18 h). Following that, the second measurements of the color coordinates were determined. The total color differences were measured, and the data were statistically analyzed (α = 0.05).</p><p><strong>Results: </strong>The temperature had a significant effect on ΔL΄ (P < 0.001), ΔC΄ (P < 0.001), and ΔH΄ (P < 0.001). The lithium disilicate restorations were more color stable than the zirconia restorations. Also, there was a significant difference (P = 0.047) between the LinkForce (2.28 ± 0.48) and Panavia SA (2.15 ± 0.46) cement. The restorations cemented at a temperature of 54°C (1.76 ± 0.11) showed significant color differences (P < 0.001) compared with those cemented at a temperature of 25°C (2.67 ± 0.15). A three-way analysis of variance (ANOVA) test revealed that the interaction between the ceramic material, cement type, and temperature had no statistically significant effect (P = 0.611) on the color stability of the ceramic restorations.</p><p><strong>Conclusions: </strong>Cement type has a significant effect on the color stability of lithium disilicate and zirconia restorations. Cement at a temperature of up to 54°C enhances the color stability of lithium disilicate and zirconia restorations.</p>\",\"PeriodicalId\":0,\"journal\":{\"name\":\"\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0,\"publicationDate\":\"2023-05-11\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"","FirstCategoryId":"1085","ListUrlMain":"","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Influence of resin cement on color stability when luting lithium disilicate and zirconia restorations. A spectrophotometry study
Aim: To evaluate the influence of resin cement on the color stability of lithium disilicate and zirconia restorations immersed in coffee after aging.
Materials and methods: Eighty maxillary premolars were classified into eight groups (n = 10) based on restorative material type (lithium disilicate or zirconia), resin cement type (G-CEM LinkForce; GC Corporation or Panavia SA Cement Plus Automix; Kuraray Noritake Dental), and preheating temperature (25°C or 54°C). Following tooth preparation, each restoration was bonded to its corresponding substrate. Using a reflectance spectrophotometer, Commission Internationale de l'Éclairage (CIE) tristimulus values were detected and calculated (D65 standard illumination, 10-degree observer angle). All specimens were aged (240,000 load cycles followed by 10,000 thermal cycles), then immersed in coffee (18 h). Following that, the second measurements of the color coordinates were determined. The total color differences were measured, and the data were statistically analyzed (α = 0.05).
Results: The temperature had a significant effect on ΔL΄ (P < 0.001), ΔC΄ (P < 0.001), and ΔH΄ (P < 0.001). The lithium disilicate restorations were more color stable than the zirconia restorations. Also, there was a significant difference (P = 0.047) between the LinkForce (2.28 ± 0.48) and Panavia SA (2.15 ± 0.46) cement. The restorations cemented at a temperature of 54°C (1.76 ± 0.11) showed significant color differences (P < 0.001) compared with those cemented at a temperature of 25°C (2.67 ± 0.15). A three-way analysis of variance (ANOVA) test revealed that the interaction between the ceramic material, cement type, and temperature had no statistically significant effect (P = 0.611) on the color stability of the ceramic restorations.
Conclusions: Cement type has a significant effect on the color stability of lithium disilicate and zirconia restorations. Cement at a temperature of up to 54°C enhances the color stability of lithium disilicate and zirconia restorations.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号