Reaction of Bacterial Poly-3-Hydroxybutyrate with Thionyl Chloride in the Presence of Zinc Chloride, and the Preparation of Chlorine-Containing Oligomers

The degradation patterns of bacterial poly-3-hydroxybutyrate (PHB) in chloroform solution under the action of thionyl chloride in the presence of zinc chloride were studied. When 2.5.mol of zinc chloride and 100 mmol of thionyl chloride were introduced into the solution of 25 mmol PHB, a decrease in the molecular weight of the polymer was observed. During the reaction, a relatively rapid decrease in the molecular weight of the polymer was noted in the first hour of the experiment; thus, the values of the weight-average molecular weight decreased from 840 kDa to 483, 167, 58.6, and 16.7 kDa after 1, 5, 24, and 96 h of the experiment, respectively. The polydispersity also gradually decreased from 2.69 at the beginning to 1.92 at the end of the experiment. Oligomers of PHB containing 3-chlorobutyric acid and 3-hydroxybutyryl chloride residues at the O and C ends of the polymer chain, respectively, were obtained. The results confirm the ability of thionyl chloride to interact with aliphatic esters in the presence of zinc compounds, and demonstrate the possibility of using this reaction to produce oligomeric derivatives of polyesters bearing chloralkyl and acid chloride functional groups.