KINETIC AND STRUCTURAL CHARACTERISTICS OF ULTRAFILTRATIONAL MEMBRANES AT SEPARATION OF SOLUTIONS CONTAINING SODIUM LAURYLSULPHATE

In work the generalized analysis of literary data on a research of relative permeability ratio of various types of porous organic and inorganic membranes was submitted. Application of a method of X-ray analysis of samples of the semipermeable ultrafiltrational membranes on a diffractometer of DRON-3 and a specific output flow on a flat-chamber ultrafiltration unit is shown. In materials of work the pilot and theoretical studies on isokinetic zones and structural characteristics of polymeric semipermeable membranes in the course of ultrafiltrational separation of the technological solutions containing the anionic and fissile surface substances are conducted. It is experimentally confirmed that kinetic curves on a specific output flow have two isokinetic zones. The first zone, the stage of the ultrafiltration process, proceeds quickly, lasts only a few minutes - 7.8 min and 13.05 min, the second zone is slower with duration of about 30 min and 60 min for ultrafiltration cellulose acetate membranes of the UAM-100 and UAM-50 series, respectively. The revealed isokinetic zones differ in characteristic times, which differ by orders of magnitude, and, as a result, the final kinetic dependence has an exponential form. The comparative analysis of roentgenograms allows to note coincidence of angles of diffraction, but significant redistribution of intensity of reflexes in air-dried and working sapless in the range of scattering angles 2θ from 8°-35°. The obtained experimental data and their comparison with literary, indicate the same set of the diffraction reflexes at corners 2θ = 17°; 22°; 25° for both samples of membranes that corresponds to the crystal reflexes of membranes created from polyamide fibers (nylon).