纳米粉体法制备无添加剂pzt52 /48陶瓷及表征

IF 0.5 4区 材料科学 Q4 MATERIALS SCIENCE, MULTIDISCIPLINARY
J. Caceres, Carlos Augusto Carlos Passos, J. V. S. Chagas
{"title":"纳米粉体法制备无添加剂pzt52 /48陶瓷及表征","authors":"J. Caceres, Carlos Augusto Carlos Passos, J. V. S. Chagas","doi":"10.1590/S1517-707620210002.1259","DOIUrl":null,"url":null,"abstract":"Lead zirconatetitanate solid solutions, Pb(Zr1-xTix)O3 – PZT, are widely recognized for representing a special group of ferroelectric materials with various potential applications in electroceramics and (micro)electronic devices. The PZT ceramics is produced by solid state reaction (conventional route) and temperatures frequently above 1200 C. As a consequence, the cost of ceramic product is expensive. Herein, we present the synthesis and processing conditions of PZT52/48 (x = 0.48) ceramics in which it was possible to lower the sintering temperature down to around 900C. We have applied a route for PZT52/48 obtaining ferroelectric ceramics through sintering of nanometric powders prepared by the polymeric precursor synthesis method (modified Pechini’s method). The sintering was achieved with a temperature of 900oC for 2 hours and the samples got 96% of their theoretical density and 1.3 m mean grain size. The electrical permittivity of the ceramic plates, studied by impedance spectroscopy, presented Curie temperature around 390 oC. Ferroelectric hysteresis measurements revealed that the remnant polarization is 3.2 μC/cm2 and coercive field is 10 kV/cm at 60 Hz. All results and characterizations have shown that the PZT samples obtained with the polymeric route are efficient as the ones prepared in the conventional SSR protocol. Keywords: PZT nanometric powder, Low temperature sintering, Dielectric properties, Ferroelectric hysteresis","PeriodicalId":18260,"journal":{"name":"Materia-rio De Janeiro","volume":"20 1","pages":""},"PeriodicalIF":0.5000,"publicationDate":"2021-03-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"Synthesis and characterization of PZT 52/48 ceramics without additives througt nanomertric powder\",\"authors\":\"J. Caceres, Carlos Augusto Carlos Passos, J. V. S. Chagas\",\"doi\":\"10.1590/S1517-707620210002.1259\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Lead zirconatetitanate solid solutions, Pb(Zr1-xTix)O3 – PZT, are widely recognized for representing a special group of ferroelectric materials with various potential applications in electroceramics and (micro)electronic devices. The PZT ceramics is produced by solid state reaction (conventional route) and temperatures frequently above 1200 C. As a consequence, the cost of ceramic product is expensive. Herein, we present the synthesis and processing conditions of PZT52/48 (x = 0.48) ceramics in which it was possible to lower the sintering temperature down to around 900C. We have applied a route for PZT52/48 obtaining ferroelectric ceramics through sintering of nanometric powders prepared by the polymeric precursor synthesis method (modified Pechini’s method). The sintering was achieved with a temperature of 900oC for 2 hours and the samples got 96% of their theoretical density and 1.3 m mean grain size. The electrical permittivity of the ceramic plates, studied by impedance spectroscopy, presented Curie temperature around 390 oC. Ferroelectric hysteresis measurements revealed that the remnant polarization is 3.2 μC/cm2 and coercive field is 10 kV/cm at 60 Hz. All results and characterizations have shown that the PZT samples obtained with the polymeric route are efficient as the ones prepared in the conventional SSR protocol. Keywords: PZT nanometric powder, Low temperature sintering, Dielectric properties, Ferroelectric hysteresis\",\"PeriodicalId\":18260,\"journal\":{\"name\":\"Materia-rio De Janeiro\",\"volume\":\"20 1\",\"pages\":\"\"},\"PeriodicalIF\":0.5000,\"publicationDate\":\"2021-03-25\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materia-rio De Janeiro\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://doi.org/10.1590/S1517-707620210002.1259\",\"RegionNum\":4,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q4\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materia-rio De Janeiro","FirstCategoryId":"88","ListUrlMain":"https://doi.org/10.1590/S1517-707620210002.1259","RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q4","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
引用次数: 0

摘要

锆钛酸铅固溶体Pb(Zr1-xTix)O3 - PZT被广泛认为是一类特殊的铁电材料,在电陶瓷和(微)电子器件中具有各种潜在的应用。PZT陶瓷是由固态反应(常规路线)和温度经常高于1200℃生产的。因此,陶瓷产品的成本昂贵。本文中,我们提出了PZT52/48 (x = 0.48)陶瓷的合成和加工条件,可以将烧结温度降低到900℃左右。我们采用了聚合前驱体合成法(改进Pechini法)制备纳米粉体烧结制备铁电陶瓷PZT52/48的途径。烧结温度为900℃,烧结时间为2小时,样品的密度达到理论密度的96%,平均晶粒尺寸为1.3m。阻抗谱法研究了陶瓷板的介电常数,发现其居里温度在390℃左右。铁电迟滞测量结果表明,残余极化为3.2 μC/cm2, 60 Hz时矫顽力场为10 kV/cm。所有结果和表征都表明,用聚合途径获得的PZT样品与用传统SSR方法制备的样品一样高效。关键词:PZT纳米粉体,低温烧结,介电性能,铁电滞后
本文章由计算机程序翻译,如有差异,请以英文原文为准。
Synthesis and characterization of PZT 52/48 ceramics without additives througt nanomertric powder
Lead zirconatetitanate solid solutions, Pb(Zr1-xTix)O3 – PZT, are widely recognized for representing a special group of ferroelectric materials with various potential applications in electroceramics and (micro)electronic devices. The PZT ceramics is produced by solid state reaction (conventional route) and temperatures frequently above 1200 C. As a consequence, the cost of ceramic product is expensive. Herein, we present the synthesis and processing conditions of PZT52/48 (x = 0.48) ceramics in which it was possible to lower the sintering temperature down to around 900C. We have applied a route for PZT52/48 obtaining ferroelectric ceramics through sintering of nanometric powders prepared by the polymeric precursor synthesis method (modified Pechini’s method). The sintering was achieved with a temperature of 900oC for 2 hours and the samples got 96% of their theoretical density and 1.3 m mean grain size. The electrical permittivity of the ceramic plates, studied by impedance spectroscopy, presented Curie temperature around 390 oC. Ferroelectric hysteresis measurements revealed that the remnant polarization is 3.2 μC/cm2 and coercive field is 10 kV/cm at 60 Hz. All results and characterizations have shown that the PZT samples obtained with the polymeric route are efficient as the ones prepared in the conventional SSR protocol. Keywords: PZT nanometric powder, Low temperature sintering, Dielectric properties, Ferroelectric hysteresis
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
Materia-rio De Janeiro
Materia-rio De Janeiro MATERIALS SCIENCE, MULTIDISCIPLINARY-
CiteScore
1.00
自引率
25.00%
发文量
51
审稿时长
6 weeks
期刊介绍: All the articles are submitted to a careful peer-reviewing evaluation process by the journal''s Editorial Board. The Editorial Board, reviewers and authors make use of a web based proprietary automated tool to deal with the reviewing procedures.the Revista Matéria''s article reviewing restricted access system - SEER. Authors are not informed about the identity of the reviewers.
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信