Synthesis of Platinum Nanoparticles from K2PtCl4 Solution Using Bacterial Cellulose Matrix

Platinum (Pt) nanoparticles have been synthesized from a precursor solution of potassium tetrachloroplatinate (K2PtCl4) using a matrix of bacterial cellulose (BC). The formation of Pt nanoparticles occurs at the surface and the inside of the BC membrane by reducing the precursor solution with a hydrogen gas reductant. The Pt nanoparticles obtained from the variations of precursor concentration, between 3 mM and 30 mM, and the formation of Pt nanoparticles have been studied using X-ray diffraction (XRD), scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDS), and thermogravimetry analysis (TGA). Based on X-ray diffraction patterns, Pt particles have sizes between 6.3 nm and 9.3 nm, and the Pt particle size increases with an increase in precursor concentration. The morphology of the Pt nanoparticles was observed by SEM-EDS and the content of Pt particles inside the membrane is higher than that on the surface of BC membranes. This analysis corresponds to the TGA analysis, but the TGA analysis is more representative in how it describes the content of Pt particles in the BC membrane.