端羧基聚氧乙烯改性聚酯的抗静电性能

Yaoming Zhao, Junwu Chen, Y. Sano, Y. Kimura
{"title":"端羧基聚氧乙烯改性聚酯的抗静电性能","authors":"Yaoming Zhao, Junwu Chen, Y. Sano, Y. Kimura","doi":"10.1002/APMC.1994.052170113","DOIUrl":null,"url":null,"abstract":"Carboxy-terminated poly(oxyethylenes) (PEO-acid) with number-average molecular weights Mn = 8400, 3300, and 1000 were used for antielectrostatic modification of poly(ethylene terephthalate) (PET). The blend PET fibers containing 2.0 and 5.0 wt.-% of PEO-acids were melt-spun at 285°C with an ordinary extruder and then drawn about 4.5-fold at 80°C. The processabilities of spinning and drawing were excellent at higher molecular weights of PEO-acid. The anti-electrostatic properties of the blend fibers became also improved with increasing molecular weight of PEO-acid. Since little ester interchange reaction took place between PET and PEO-acid during meltspinning, the blend fibers could retain almost the same mechanical properties as the original PET fiber. \n \n \n \nCarboxy-terminierte Polyoxyethylene (PEO-acid) mit zahlenmittleren Molekulargewichten Mn = 8400, 3300 und 1000 wurden zur antielektrostatischen Modifizierung von Polyethylenterephthalat (PET) verwendet. Fasern aus PET-PEO-acid-Blends mit 2,0 oder 5,0 Gew.-% PEO-acid wurden bei 285°C mit einem normalen Extruder aus der Schmelze gesponnen und anschliesend bei 80°C um das ca. 4,5fache verstreckt. Die Verarbeitbarkeit beim Verspinnen und Verstrecken war bei Verwendung von PEO-acid mit hohen Molekulargewichten ausgezeichnet. Die anti-elektrostatischen Eigenschaften wurden ebenfalls mit steigendem PEO-acid-Molekulargewicht besser. Da eine Umesterung beim Verspinnen nur in geringem Ausmas stattfand, blieben die mechanischen Eigenschaften der Blend-Fasern gegenuber den PET-Fasern nahezu unverandert.","PeriodicalId":7808,"journal":{"name":"Angewandte Makromolekulare Chemie","volume":"68 1","pages":"129-137"},"PeriodicalIF":0.0000,"publicationDate":"1994-04-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"4","resultStr":"{\"title\":\"Antistatic modification of polyester with carboxyterminated poly(oxyethylene)\",\"authors\":\"Yaoming Zhao, Junwu Chen, Y. Sano, Y. Kimura\",\"doi\":\"10.1002/APMC.1994.052170113\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Carboxy-terminated poly(oxyethylenes) (PEO-acid) with number-average molecular weights Mn = 8400, 3300, and 1000 were used for antielectrostatic modification of poly(ethylene terephthalate) (PET). The blend PET fibers containing 2.0 and 5.0 wt.-% of PEO-acids were melt-spun at 285°C with an ordinary extruder and then drawn about 4.5-fold at 80°C. The processabilities of spinning and drawing were excellent at higher molecular weights of PEO-acid. The anti-electrostatic properties of the blend fibers became also improved with increasing molecular weight of PEO-acid. Since little ester interchange reaction took place between PET and PEO-acid during meltspinning, the blend fibers could retain almost the same mechanical properties as the original PET fiber. \\n \\n \\n \\nCarboxy-terminierte Polyoxyethylene (PEO-acid) mit zahlenmittleren Molekulargewichten Mn = 8400, 3300 und 1000 wurden zur antielektrostatischen Modifizierung von Polyethylenterephthalat (PET) verwendet. Fasern aus PET-PEO-acid-Blends mit 2,0 oder 5,0 Gew.-% PEO-acid wurden bei 285°C mit einem normalen Extruder aus der Schmelze gesponnen und anschliesend bei 80°C um das ca. 4,5fache verstreckt. Die Verarbeitbarkeit beim Verspinnen und Verstrecken war bei Verwendung von PEO-acid mit hohen Molekulargewichten ausgezeichnet. Die anti-elektrostatischen Eigenschaften wurden ebenfalls mit steigendem PEO-acid-Molekulargewicht besser. Da eine Umesterung beim Verspinnen nur in geringem Ausmas stattfand, blieben die mechanischen Eigenschaften der Blend-Fasern gegenuber den PET-Fasern nahezu unverandert.\",\"PeriodicalId\":7808,\"journal\":{\"name\":\"Angewandte Makromolekulare Chemie\",\"volume\":\"68 1\",\"pages\":\"129-137\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"1994-04-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"4\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Angewandte Makromolekulare Chemie\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.1002/APMC.1994.052170113\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Angewandte Makromolekulare Chemie","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.1002/APMC.1994.052170113","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
引用次数: 4

摘要

采用数均分子量Mn = 8400、3300和1000的端羧基聚氧乙烯(peo -酸)对聚对苯二甲酸乙酯(PET)进行抗静电改性。将peo -酸含量分别为2.0 wt.-%和5.0 wt.-%的共混PET纤维在285℃下用普通挤出机熔融纺丝,然后在80℃下拉伸约4.5倍。在高分子量peo -酸条件下,纺丝和拉伸工艺性能优异。随着peo酸分子量的增加,共混纤维的抗静电性能也得到了改善。由于熔融纺丝过程中PET与peo -酸之间几乎没有酯交换反应,因此共混纤维可以保持与原PET纤维基本相同的力学性能。羧基末端聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯(peo -酸)聚氧乙烯Fasern - pet - peo -acid- blend: 2000到5000加仑。-% peo -酸性木浆,温度为285°C,在正常条件下挤压,温度为80°C。Verarbeitbarkeit bem Verspinnen和verstrecen war bei Verwendung von PEO-acid mit hohen molecular genergewitten ausgezeichnet。抗静电特性的研究与应用。[3] [1] [3] [1] [3] [1] [3] [1] [3] [1] [2] [1] [2] [1] [3]
本文章由计算机程序翻译,如有差异,请以英文原文为准。
Antistatic modification of polyester with carboxyterminated poly(oxyethylene)
Carboxy-terminated poly(oxyethylenes) (PEO-acid) with number-average molecular weights Mn = 8400, 3300, and 1000 were used for antielectrostatic modification of poly(ethylene terephthalate) (PET). The blend PET fibers containing 2.0 and 5.0 wt.-% of PEO-acids were melt-spun at 285°C with an ordinary extruder and then drawn about 4.5-fold at 80°C. The processabilities of spinning and drawing were excellent at higher molecular weights of PEO-acid. The anti-electrostatic properties of the blend fibers became also improved with increasing molecular weight of PEO-acid. Since little ester interchange reaction took place between PET and PEO-acid during meltspinning, the blend fibers could retain almost the same mechanical properties as the original PET fiber. Carboxy-terminierte Polyoxyethylene (PEO-acid) mit zahlenmittleren Molekulargewichten Mn = 8400, 3300 und 1000 wurden zur antielektrostatischen Modifizierung von Polyethylenterephthalat (PET) verwendet. Fasern aus PET-PEO-acid-Blends mit 2,0 oder 5,0 Gew.-% PEO-acid wurden bei 285°C mit einem normalen Extruder aus der Schmelze gesponnen und anschliesend bei 80°C um das ca. 4,5fache verstreckt. Die Verarbeitbarkeit beim Verspinnen und Verstrecken war bei Verwendung von PEO-acid mit hohen Molekulargewichten ausgezeichnet. Die anti-elektrostatischen Eigenschaften wurden ebenfalls mit steigendem PEO-acid-Molekulargewicht besser. Da eine Umesterung beim Verspinnen nur in geringem Ausmas stattfand, blieben die mechanischen Eigenschaften der Blend-Fasern gegenuber den PET-Fasern nahezu unverandert.
求助全文
通过发布文献求助,成功后即可免费获取论文全文。 去求助
来源期刊
自引率
0.00%
发文量
0
×
引用
GB/T 7714-2015
复制
MLA
复制
APA
复制
导出至
BibTeX EndNote RefMan NoteFirst NoteExpress
×
提示
您的信息不完整,为了账户安全,请先补充。
现在去补充
×
提示
您因"违规操作"
具体请查看互助需知
我知道了
×
提示
确定
请完成安全验证×
copy
已复制链接
快去分享给好友吧!
我知道了
右上角分享
点击右上角分享
0
联系我们:info@booksci.cn Book学术提供免费学术资源搜索服务,方便国内外学者检索中英文文献。致力于提供最便捷和优质的服务体验。 Copyright © 2023 布克学术 All rights reserved.
京ICP备2023020795号-1
ghs 京公网安备 11010802042870号
Book学术文献互助
Book学术文献互助群
群 号:481959085
Book学术官方微信