A new approach for the preparation of cellulose nanocrystals from bamboo pulp through extremely low acid hydrolysis

As a renewable and biodegradable nanomaterial, cellulose nanocrystal (CNC) has a wide range of potential applications, but production of CNC faces significant challenges in capital investment and manufacturing cost. In this work, the one-step preparation of CNC from bleached kraft bamboo pulp by extremely low acid (concentration of acid ≤ 0.1 wt%) hydrolysis was demonstrated. The experimental data indicated that the yield of CNC was strongly affected by the operating pressure and concentration of hydrochloric acid (HCl), as well as temperature. Rod-like CNC with a mean particle size of 524 nm was obtained through an extremely low acid (ELA) hydrolysis process. The yield of CNC can reach to 37.1% by an ELA hydrolysis process at 180°C for 60 min with 0.08 wt% HCl and 20 MPa operating pressure. The Fourier transform-infrared spectroscopy (FTIR) measurements show that the as-pre-pared CNC maintained cellulose structure. Compared with a conventional CNC prepared by strong sulfuric acid (H2SO4) hydrolysis, the CNC prepared by ELA hydrolysis process exhibited much higher thermal stability.