{"title":"回火温度对X70双相钢组织和力学性能的影响","authors":"Zidelmel Sami, Al-Zuhairi Omar","doi":"10.30544/753","DOIUrl":null,"url":null,"abstract":"This study uses direct quenching (DQ) heat treatment at an intercritical annealing temperature (IAT) of 800 °C to form a martensite-ferrite dual phase microstructure of X70 steel. The effects of tempering temperatures ranging from 200 to 500 °C on tensile properties in a dual-phase X70 steel are investigated. Carbon diffusion and redistribution in the microstructure are influenced by tempering. It was discovered that the amount of carbides increases with the tempered temperature, resulting in depleted carbon in martensite. Conversely, increasing the tempered temperature causes a decrease in ultimate tensile strength and yield strength while increasing elongation.","PeriodicalId":18466,"journal":{"name":"Metallurgical and Materials Engineering","volume":"32 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2022-06-30","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"Effects of the tempering temperature on microstructure and mechanical properties of X70 dual phase steel\",\"authors\":\"Zidelmel Sami, Al-Zuhairi Omar\",\"doi\":\"10.30544/753\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"This study uses direct quenching (DQ) heat treatment at an intercritical annealing temperature (IAT) of 800 °C to form a martensite-ferrite dual phase microstructure of X70 steel. The effects of tempering temperatures ranging from 200 to 500 °C on tensile properties in a dual-phase X70 steel are investigated. Carbon diffusion and redistribution in the microstructure are influenced by tempering. It was discovered that the amount of carbides increases with the tempered temperature, resulting in depleted carbon in martensite. Conversely, increasing the tempered temperature causes a decrease in ultimate tensile strength and yield strength while increasing elongation.\",\"PeriodicalId\":18466,\"journal\":{\"name\":\"Metallurgical and Materials Engineering\",\"volume\":\"32 1\",\"pages\":\"\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2022-06-30\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Metallurgical and Materials Engineering\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.30544/753\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Metallurgical and Materials Engineering","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.30544/753","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
Effects of the tempering temperature on microstructure and mechanical properties of X70 dual phase steel
This study uses direct quenching (DQ) heat treatment at an intercritical annealing temperature (IAT) of 800 °C to form a martensite-ferrite dual phase microstructure of X70 steel. The effects of tempering temperatures ranging from 200 to 500 °C on tensile properties in a dual-phase X70 steel are investigated. Carbon diffusion and redistribution in the microstructure are influenced by tempering. It was discovered that the amount of carbides increases with the tempered temperature, resulting in depleted carbon in martensite. Conversely, increasing the tempered temperature causes a decrease in ultimate tensile strength and yield strength while increasing elongation.
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号