Compression set and damping properties of oil-extended elastomers for sealants production

Damping materials have been widely used in the vibration and noise control to reduce their harmful consequences in different areas such as their application in the drilling equipment, aerospace and naval vessels, transportation vehicles, bridges and high buildings. Because of severe environmental standards, the oil fabrication is developing synthetic environmentally friendly drilling fluids. For a vehicle, applications are produced: the outer and inner beltline seals and the glass run channel. The compression set is the important characteristic of elastomeric sealing materials as spontaneous stress release during applica tion due to the internal pressure or external forces variations. The temperatureand frequency-insensitive damping are of significance for industrial uses. Elastomeric hybrid materials based on terpolymers as network precursor are very common for sealants fabrication. The focus of this work was to prepare oil-extended elastomeric hybrid materials based on ethylenepropylene-diene monomer rubber (EPDM), ground calcium carbonate and furnace nano carbon black. Cure characteristics were carried out on oscillating disc rheometer. The crosslinking of rubber compounds was performed in a molding press. The compression set was assessed using the standard procedure. The morphology of the cryogenically fractured surface of samples with different content of paraffin oil was characterized by scanning electron microscopy (SEM). Mechanical properties and hardness were analyzed before and after the aging of obtained samples. Damping properties of prepared materialswere determined using bending mode. The loss tangent, tan δ, was used as a measure of vibration energy dissipation.