{"title":"致密化时间对桦木单板抗拉强度和弹性模量的影响","authors":"Adam Słupecki, Anita Wronka","doi":"10.5604/01.3001.0016.0488","DOIUrl":null,"url":null,"abstract":"The influence of densification time on the tensile strength and modulus of elasticity of birch veneers. The aim of the following study was to examine and compare tensile strength, modulus of elasticity, and thickness of birch (Betula pendula Roth) veneers modified by thermomechanical densification. Birch veneers were densified at the temperature of 100 °C at different times (ranges from 10 to 60 minutes). Tensile strength was tested longitudinally to the grain. As a result of this study change in tensile strength was observed for 60 minutes of densification. The rise in modulus of elasticity was also observed for 10, 20, 30, 50, and 60 minutes. The thickness of wooden veneers was changed significantly for each densification time\n\n","PeriodicalId":8020,"journal":{"name":"Annals of WULS, Forestry and Wood Technology","volume":"39 1","pages":""},"PeriodicalIF":0.0000,"publicationDate":"2022-07-25","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"1","resultStr":"{\"title\":\"The influence of densification time on the tensile strength and modulus of elasticity of birch veneers\",\"authors\":\"Adam Słupecki, Anita Wronka\",\"doi\":\"10.5604/01.3001.0016.0488\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"The influence of densification time on the tensile strength and modulus of elasticity of birch veneers. The aim of the following study was to examine and compare tensile strength, modulus of elasticity, and thickness of birch (Betula pendula Roth) veneers modified by thermomechanical densification. Birch veneers were densified at the temperature of 100 °C at different times (ranges from 10 to 60 minutes). Tensile strength was tested longitudinally to the grain. As a result of this study change in tensile strength was observed for 60 minutes of densification. The rise in modulus of elasticity was also observed for 10, 20, 30, 50, and 60 minutes. The thickness of wooden veneers was changed significantly for each densification time\\n\\n\",\"PeriodicalId\":8020,\"journal\":{\"name\":\"Annals of WULS, Forestry and Wood Technology\",\"volume\":\"39 1\",\"pages\":\"\"},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2022-07-25\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"1\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Annals of WULS, Forestry and Wood Technology\",\"FirstCategoryId\":\"1085\",\"ListUrlMain\":\"https://doi.org/10.5604/01.3001.0016.0488\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"\",\"JCRName\":\"\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Annals of WULS, Forestry and Wood Technology","FirstCategoryId":"1085","ListUrlMain":"https://doi.org/10.5604/01.3001.0016.0488","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"","JCRName":"","Score":null,"Total":0}
The influence of densification time on the tensile strength and modulus of elasticity of birch veneers
The influence of densification time on the tensile strength and modulus of elasticity of birch veneers. The aim of the following study was to examine and compare tensile strength, modulus of elasticity, and thickness of birch (Betula pendula Roth) veneers modified by thermomechanical densification. Birch veneers were densified at the temperature of 100 °C at different times (ranges from 10 to 60 minutes). Tensile strength was tested longitudinally to the grain. As a result of this study change in tensile strength was observed for 60 minutes of densification. The rise in modulus of elasticity was also observed for 10, 20, 30, 50, and 60 minutes. The thickness of wooden veneers was changed significantly for each densification time
求助内容：
应助结果提醒方式：
京公网安备 11010802042870号