求助PDF
{"title":"P(BAMO/AMMO)基含能热塑性聚氨酯弹性体的性能研究","authors":"王刚, 葛震, 罗运军","doi":"10.11943/J.ISSN.1006-9941.2015.10.003","DOIUrl":null,"url":null,"abstract":"分别采用基团加和法和燃烧热法得到含不同聚(3,3'-双(叠氮甲基)氧杂环丁烷)(PBAMO)和氨基甲酸酯硬段含量P(BAMO/AMMO)基含能热塑性聚氨酯弹性体(ETPE)的生成热。研究了PBAMO、氨基甲酸酯硬段的含量对ETPE生成热的影响。采用最小自由能法优选出一组P(BAMO/AMMO)ETPE基推进剂配方。计算了理论比冲。测试了P(BAMO/AMMO)ETPE基推进剂的静态拉伸强度、断裂延伸率、摩擦感度、撞击感度和燃速压力指数。结果表明,随着PBAMO质量的增加、氨基甲酸酯硬段含量的降低,P(BAMO/AMMO)ETPE的生成热增加。优选的15/5/20/38.5/18/3.5-P(BAMO/AMMO)/Bu-NENA/RDX/AP/Al/催化剂推进剂的理论比冲为2699.51 N·s·kg-1(燃烧室压强为10 MPa)。此推进剂的静态拉伸强度为1.22 MPa,断裂延伸率为11.37%。包覆固体填料可显著降低推进剂预混物料的机械感度,使特性落高H50增加37 cm,摩擦感度下降36%,6~15 MPa压力范围内的燃速压力指数n=0.37。","PeriodicalId":35753,"journal":{"name":"Hanneng Cailiao/Chinese Journal of Energetic Materials","volume":null,"pages":null},"PeriodicalIF":0.0000,"publicationDate":"2015-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"P(BAMO/AMMO)基含能热塑性聚氨酯弹性体的性能研究\",\"authors\":\"王刚, 葛震, 罗运军\",\"doi\":\"10.11943/J.ISSN.1006-9941.2015.10.003\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"分别采用基团加和法和燃烧热法得到含不同聚(3,3'-双(叠氮甲基)氧杂环丁烷)(PBAMO)和氨基甲酸酯硬段含量P(BAMO/AMMO)基含能热塑性聚氨酯弹性体(ETPE)的生成热。研究了PBAMO、氨基甲酸酯硬段的含量对ETPE生成热的影响。采用最小自由能法优选出一组P(BAMO/AMMO)ETPE基推进剂配方。计算了理论比冲。测试了P(BAMO/AMMO)ETPE基推进剂的静态拉伸强度、断裂延伸率、摩擦感度、撞击感度和燃速压力指数。结果表明,随着PBAMO质量的增加、氨基甲酸酯硬段含量的降低,P(BAMO/AMMO)ETPE的生成热增加。优选的15/5/20/38.5/18/3.5-P(BAMO/AMMO)/Bu-NENA/RDX/AP/Al/催化剂推进剂的理论比冲为2699.51 N·s·kg-1(燃烧室压强为10 MPa)。此推进剂的静态拉伸强度为1.22 MPa,断裂延伸率为11.37%。包覆固体填料可显著降低推进剂预混物料的机械感度,使特性落高H50增加37 cm,摩擦感度下降36%,6~15 MPa压力范围内的燃速压力指数n=0.37。\",\"PeriodicalId\":35753,\"journal\":{\"name\":\"Hanneng Cailiao/Chinese Journal of Energetic Materials\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":0.0000,\"publicationDate\":\"2015-01-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Hanneng Cailiao/Chinese Journal of Energetic Materials\",\"FirstCategoryId\":\"1087\",\"ListUrlMain\":\"https://doi.org/10.11943/J.ISSN.1006-9941.2015.10.003\",\"RegionNum\":0,\"RegionCategory\":null,\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q3\",\"JCRName\":\"Engineering\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Hanneng Cailiao/Chinese Journal of Energetic Materials","FirstCategoryId":"1087","ListUrlMain":"https://doi.org/10.11943/J.ISSN.1006-9941.2015.10.003","RegionNum":0,"RegionCategory":null,"ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q3","JCRName":"Engineering","Score":null,"Total":0}
引用次数: 0
引用
批量引用
摘要
分别采用基团加和法和燃烧热法得到含不同聚(3,3'-双(叠氮甲基)氧杂环丁烷)(PBAMO)和氨基甲酸酯硬段含量P(BAMO/AMMO)基含能热塑性聚氨酯弹性体(ETPE)的生成热。研究了PBAMO、氨基甲酸酯硬段的含量对ETPE生成热的影响。采用最小自由能法优选出一组P(BAMO/AMMO)ETPE基推进剂配方。计算了理论比冲。测试了P(BAMO/AMMO)ETPE基推进剂的静态拉伸强度、断裂延伸率、摩擦感度、撞击感度和燃速压力指数。结果表明,随着PBAMO质量的增加、氨基甲酸酯硬段含量的降低,P(BAMO/AMMO)ETPE的生成热增加。优选的15/5/20/38.5/18/3.5-P(BAMO/AMMO)/Bu-NENA/RDX/AP/Al/催化剂推进剂的理论比冲为2699.51 N·s·kg-1(燃烧室压强为10 MPa)。此推进剂的静态拉伸强度为1.22 MPa,断裂延伸率为11.37%。包覆固体填料可显著降低推进剂预混物料的机械感度,使特性落高H50增加37 cm,摩擦感度下降36%,6~15 MPa压力范围内的燃速压力指数n=0.37。
本文章由计算机程序翻译,如有差异,请以英文原文为准。
P(BAMO/AMMO)基含能热塑性聚氨酯弹性体的性能研究
分别采用基团加和法和燃烧热法得到含不同聚(3,3'-双(叠氮甲基)氧杂环丁烷)(PBAMO)和氨基甲酸酯硬段含量P(BAMO/AMMO)基含能热塑性聚氨酯弹性体(ETPE)的生成热。研究了PBAMO、氨基甲酸酯硬段的含量对ETPE生成热的影响。采用最小自由能法优选出一组P(BAMO/AMMO)ETPE基推进剂配方。计算了理论比冲。测试了P(BAMO/AMMO)ETPE基推进剂的静态拉伸强度、断裂延伸率、摩擦感度、撞击感度和燃速压力指数。结果表明,随着PBAMO质量的增加、氨基甲酸酯硬段含量的降低,P(BAMO/AMMO)ETPE的生成热增加。优选的15/5/20/38.5/18/3.5-P(BAMO/AMMO)/Bu-NENA/RDX/AP/Al/催化剂推进剂的理论比冲为2699.51 N·s·kg-1(燃烧室压强为10 MPa)。此推进剂的静态拉伸强度为1.22 MPa,断裂延伸率为11.37%。包覆固体填料可显著降低推进剂预混物料的机械感度,使特性落高H50增加37 cm,摩擦感度下降36%,6~15 MPa压力范围内的燃速压力指数n=0.37。